LNP™ STAT-KON™ EX07311P compound
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | grpyUO_LNP-STAT-KON-EX07311P-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON* EX07311P is an easy flowing ESD-safe compound based on Polyetherimide resin. This compound is developed for good dimensional stability for use in ESD Tray for Backend Semicon and HDD tray applications. Also known as: LNP* STAT-KON* Compound EX07311P (SER) Product reorder name: EX07311P |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.56 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Volume-Flow Rate (MVR) (345°C/10.0 kg) | 30.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Flow | 0.29 | % | |
| Across Flow | 0.36 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 15000 | MPa | ASTM D638 |
| -- | 15200 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 175 | MPa | ASTM D638 |
| Break | 174 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 2.1 | % | ASTM D638 |
| Break | 1.9 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 11500 | MPa | ASTM D790 |
| -- 5 | 13200 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 203 | MPa | ISO 178 |
| Break, 50.0 mm Span 6 | 200 | MPa | ASTM D790 |
| Coefficient of Friction (vs. Itself - Dynamic) | 0.40 | ASTM D3702 Modified | |
| Flexural Strain at Break 7 | 1.7 | % | ISO 178 |
| Wear Factor - Washer | 20.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 56 | J/m | ASTM D256 |
| 23°C 8 | 6.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 202 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 9 | 204 | °C | ISO 75-2/Af |
| CLTE | ASTM E831 | ||
| Flow : -40 to 40°C | 8.9E-6 | cm/cm/°C | |
| Transverse : -40 to 40°C | 4.4E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+5 to 1.0E+6 | ohms | ASTM D257, IEC 60093 |
| Volume Resistivity | 1.0E+5 to 1.0E+6 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Drying Time, Maximum | 24 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 60 | % | |
| Rear Temperature | 332 to 399 | °C | |
| Middle Temperature | 338 to 399 | °C | |
| Front Temperature | 343 to 399 | °C | |
| Nozzle Temperature | 343 to 399 | °C | |
| Processing (Melt) Temp | 349 to 399 | °C | |
| Mold Temperature | 135 to 163 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.025 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Wellamid® GF13-66 XE-N | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| Viton® VTR-9176 | DuPont Performance Elastomers | Fluorelastomer | Viton® |
| Generic PPE+PS - Glass Fiber, Milled | Generic | PPE+PS | Generic |
| OmniLon™ PA6/6 GR43 | OMNI Plastics, LLC | Nylon 66 | OmniLon™ |
| Panlite® L-1225L | TEIJIN LIMITED | PC | Panlite® |