SLOVAMID® 66 GF 15 T 6 TS
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Plastcom |
| Trademark: | SLOVAMID® 66 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gqyLma_SLOVAMID-66-GF-15-T-6-TS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Chemically reinforced with 15% glass fibre and 6% of talc, suitable for mouldings with high strength and toughness also at low temperatures. Used in the automotive, engineering and electrical industry. With the content of GF also the toughness, flexural and tensile strength increase, the shrinkage decreases and the heat application increases up to 150°C. It achieves higher rates of tensile strength and modulus of elasticity also in conditioning state when compared with PA 6 GF. Application: hobby tools, covers of electrotools, electromotors, cooling screws of blowers, gear wheels, carrying parts in the automotive industry like eg. brake cables. Delivered in natural and in the full RAL colour scale. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.29 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (275°C/0.325 kg) | 3.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | STM 64 0808 | ||
| Across Flow | 1.2 | % | |
| Flow | 0.80 | % | |
| Water Content | 0.15 | % | ISO 960 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5800 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 115 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 2.6 | % | ISO 527-2 |
| Flexural Modulus | 4700 | MPa | ISO 178 |
| Flexural Stress | 175 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20°C | 3.5 | kJ/m² | |
| 23°C | 4.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -20°C | 40 | kJ/m² | |
| 23°C | 40 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 250 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 250 | °C | ISO 306/B |
| Melting Temperature (DSC) | 260 | °C | ISO 3146 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C | |
| Injection Pressure | 70.0 to 120 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polystyrene Crystal 1441 | TOTAL Refining & Chemicals | PS (GPPS) | TOTAL Polystyrene |
| Petlon Prime B1-G25-00-NT | Petlon Polymers Ltd | Nylon 6 | Petlon Prime |
| Plaslube® PC GF20 TL10 BK | Techmer Engineered Solutions | PC | Plaslube® |
| Sylvin 9048-100 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Durethan® BKV 115 H2.0 DUS008 000000 | LANXESS GmbH | Nylon 6 | Durethan® |