Unigel PS U8854
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | Unigel Plásticos |
| Trademark: | Unigel PS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gqnuRC_Unigel-PS-U8854.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 8.5 | g/10 min | ASTM D1238 |
| Water Absorption (Equilibrium) | 0.070 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2000 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 20.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | > 40 | % | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.50 mm) | 90 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.30 mm) | 80.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 88.0 | °C | ASTM D1525 1 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ACCUTECH™ NY0730G30L1 | ACLO Compounders Inc. | Nylon 6 | ACCUTECH™ |
| AKROMID® B3 3 S3 10 natural (1808) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| CALP MRP440 | Lion Idemitsu Composites Co., Ltd. | Polyolefin, Unspecified | CALP |
| Karina CLEAR PVC COMPOUND 80/202-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| PIVINEL™ 116-80H-LF | HELLENIC CABLES S.A. | PVC, Unspecified | PIVINEL™ |