Spartech Polycom PP6140 A2
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Spartech Polycom |
| Trademark: | Spartech |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gqiEVi_Spartech-Polycom-PP6140-A2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 40% Talc Filled, Impact Modified, Natural, Homopolymer Polypropylene compound offers high level of stiffness balanced with moderate impact resistance and excellent processibility. A Polycom Huntsman Inc. representative can provide futher infomation on this and other Polycom Huntsman Inc. products. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.24 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 1.0 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 29.0 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 5.0 | % | ASTM D638 |
| Fracture | 15 | % | ASTM D638 |
| Flexural Modulus - Secant | 2070 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 53 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 127 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 68.3 | °C | ASTM D648 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SAXAMID™ 136F6Q32 | SAX Polymers | Nylon 6 | SAXAMID™ |
| Solef® 6010 | Solvay Specialty Polymers | PVDF | Solef® |
| Monprene® MP-1079 | Teknor Apex Company | TPE | Monprene® |
| WELLAMID Nylon 6000 MR 209 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 6 | WELLAMID Nylon |
| INLUBE PA6GF30TF13SI2 | Infinity LTL Engineered Compounds | Nylon 6 | INLUBE |