RTP 1103 TFE 15
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gqdY7d_RTP-1103-TFE-15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. -Preliminary Product Data per RTP Co.- This material offers an excellent balance of strength, heat resistance and toughness in a water resistant composite. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.59 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.20 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.050 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7920 | MPa | ASTM D638 |
| Tensile Strength | 96.5 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.0 | % | ASTM D638 |
| Flexural Modulus | 6890 | MPa | ASTM D790 |
| Flexural Strength | 159 | MPa | ASTM D790 |
| Compressive Strength | 138 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 80 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 430 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 251 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 57.0 | °C | ASTM D648 |
| CLTE - Flow | 3.2E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.27 | W/m/K | ASTM C177 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.59 mm, Values per RTP Company testing.) | HB | UL 94 |
| Additional Information |
|---|
| Mold Shrinkage, Linear-Flow, ASTM D-955, 0.25in.: 4mil/in. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 135 | °C | |
| Drying Time | 3.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 232 - 271 | °C | |
| Middle Temperature | 232 - 271 | °C | |
| Front Temperature | 232 - 271 | °C | |
| Processing (Melt) Temp | 288 | °C | |
| Mold Temperature | 38.0 - 121 | °C | |
| Injection Pressure | 68.9 - 103 | MPa | |
| Back Pressure | 0.172 - 0.517 | MPa | |
| Clamp Tonnage | 6.9 - 11 | kN/cm² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Toyolac® 700 314 | Toray Plastics (Malaysia) Sdn. Bhd. | ABS | Toyolac® |
| 3M™ Dyneon™ Fluoroplastic FEP 6322Z | 3M Advanced Materials Division | FEP | 3M™ Dyneon™ Fluoroplastic |
| Bolv ABS | Shandong Jining Bolv Chemicals Co.,Ltd | ABS | Bolv |
| Bormed™ HD800CF-11 | Borealis AG | PP Homopolymer | Bormed™ |
| Electrafil® J-80/CF/20 NAT | Techmer Engineered Solutions | Acetal (POM) Copolymer | Electrafil® |