LG ABS PT270
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | LG ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gqZWgW_LG-ABS-PT270.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description: Good Paintability Application: Exterior Part of Automobile and Motor cycle |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.02 - 1.03 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 29 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 - 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 100 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1(3.20 mm) | 1660 | MPa | ASTM D638 |
| Tensile Strength 2(Yield, 3.20 mm) | 39.2 | MPa | ASTM D638 |
| Tensile Elongation 3(Break, 3.20 mm) | > 10 | % | ASTM D638 |
| Flexural Modulus 4(3.20 mm) | 2160 | MPa | ASTM D790 |
| Flexural Strength 5(3.20 mm) | 62.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 3.20 mm | 250 | J/m | ASTM D256 |
| -30°C, 6.40 mm | 250 | J/m | ASTM D256 |
| 23°C, 3.20 mm | 390 | J/m | ASTM D256 |
| 23°C, 6.40 mm | 350 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm | 87.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 85.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 91.0 | °C | ASTM D1525 6 |
| RTI Elec | 60.0 | °C | UL 746 |
| RTI Imp | 60.0 | °C | UL 746 |
| RTI | 60.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 180 - 200 | °C | |
| Middle Temperature | 190 - 210 | °C | |
| Front Temperature | 200 - 220 | °C | |
| Nozzle Temperature | 200 - 230 | °C | |
| Processing (Melt) Temp | 210 - 240 | °C | |
| Mold Temperature | 40.0 - 70.0 | °C | |
| Back Pressure | 0.981 - 1.96 | MPa | |
| Screw Speed | 10 - 20 | rpm |
| Injection instructions |
|---|
| Minimum Moisture Content: 0.01% |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 15 mm/min |
| 5 . | 15 mm/min |
| 6 . | 速率 A (50°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHLEN H4252 | DAEHA Co., LTD | PP, Unspecified | TECHLEN |
| Epoxies, Ect. 50-3170 | Epoxies, Etc. | Epoxy | Epoxies, Ect. |
| Kepital® F10-01 | Korea Engineering Plastics Co., Ltd | Acetal (POM) Copolymer | Kepital® |
| Jackdaw PP EW16NT6686 | Jackdaw Polymers | PP, Unspecified | Jackdaw PP |
| OTECH ALLOY OT09060LSZH - Riser Jacket | OTECH Corporation | TP, Unspecified | OTECH ALLOY |