FRAGOM G/991 XA
| Category: | Polyolefin, Unspecified , Polyolefin |
| Manufacturer: | Crosspolimeri S.p.A. |
| Trademark: | FRAGOM |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gq0y4l_FRAGOM-G-991-XA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
FRAGOM is the trade-mark of our flame retardant halogen free polyolefine compounds. FRAGOM G/991 XA flame retardant crosslinkable compound having GOOD RESISTANCE TO OIL for insulation and sheathing. It is a conveniently grafted compound able to react in presence of moisture and of a catalyst. We normally suggest our catalyst type MAC/100 SCU. To use in solar cables sheathing (TUV) we suggest to add 10-11 % of catalyst MAC/500 REACTION BETWEEN GRAFTING AND CATALYST These two compounds, separately stored, must be mixed before starting extrusion in the ratio: GRAFTING/CATALYST 95/5 CERTIFY VDE 0207-24 HM3, BS 7655 EI5, CEI 2011 M2, IEC 60092-359 SHF2 |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.40 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/21.6 kg) | 7.0 - 12 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 45 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | > 13.0 | MPa | IEC 60811 |
| Tensile Strain (Break) | > 250 | % | IEC 60811 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air | IEC 60811 | ||
| 127°C, 40 hr 1 | 15 | % | IEC 60811 |
| 135°C, 168 hr 2 | 20 | % | IEC 60811 |
| Change in Tensile Strain at Break in Air | IEC 60811 | ||
| 127°C, 40 hr 3 | -7.0 | % | IEC 60811 |
| 135°C, 168 hr 4 | -10 | % | IEC 60811 |
| Change in Tensile Strength | IEC 60811 | ||
| 70°C, 168 hr 5 | -10 | % | IEC 60811 |
| 100°C, 168 hr 6 | -20 | % | IEC 60811 |
| Change in Ultimate Elongation | IEC 60811 | ||
| 70°C, 168 hr 7 | -15 | % | IEC 60811 |
| 100°C, 168 hr 8 | -19 | % | IEC 60811 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset 9 | IEC 60811 | ||
| 250°C | 70 | % | IEC 60811 |
| Residual : 250°C | 5.0 | % | IEC 60811 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Conductivity | µS/mm | IEC 60754-2 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Halogen Content | % | IEC 60754-1 | |
| Toxicity- pH | > 4.30 | IEC 60754-2 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Head Temperature | 205 | °C |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 32 | % | ASTM D2863 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 150 | °C | |
| Cylinder Zone 2 Temp. | 170 | °C | |
| Cylinder Zone 3 Temp. | 180 | °C | |
| Cylinder Zone 4 Temp. | 195 | °C | |
| Die Temperature | 215 | °C |
| Extrusion instructions |
|---|
| Crosslinking of the finished product is obtained by: Immersion in hot water at 80/85°C. Steam treatment at 0,15 bar. Ambient air crosslinking at natural temperature and moisture, after a right number of days depending on climatic conditions. |
| Note Message | |
|---|---|
| 1 . | Air Bomb |
| 2 . | Heat Aging |
| 3 . | Air Bomb |
| 4 . | Heat Aging |
| 5 . | Aging in IRM 903 oil |
| 6 . | Aging in IRM 902 oil |
| 7 . | Aging in IRM 903 oil |
| 8 . | Aging in IRM 902 oil |
| 9 . | 20 N/cm² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SFE4000 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| Starflam AFR460B | Eurostar Engineering Plastics | Nylon 66 | Starflam |
| TAIRILAC AF3535 | Formosa Plastics Corporation | ABS | TAIRILAC |
| Chemlon® 415 G | Teknor Apex Company (Chem Polymer) | Nylon 6 | Chemlon® |
| EPAMOULD 675A01 | Epaflex Polyurethanes S.R.L. | TPU-Polyester | EPAMOULD |