Aurora PVC AP2282 Series
| Category: | PVC, Unspecified , Polyvinyl Chloride |
| Manufacturer: | Aurora Plastics, Inc. |
| Trademark: | Aurora PVC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gpdaUM_Aurora-PVC-AP2282-Series.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
A high rate, high impact PVC powder, extrusion compound, for interior applications as well as substrates. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.45 to 1.49 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 22°C) | 77 to 83 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (22°C) | 2480 | MPa | ASTM D638 |
| Tensile Strength (Yield, 22°C) | 42.1 | MPa | ASTM D638 |
| Flexural Modulus (22°C) | 2960 | MPa | ASTM D790 |
| Flexural Strength (22°C) | 79.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| 0°C | 100 | J/m | |
| 23°C | 270 | J/m | |
| Drop Impact Resistance | ASTM D4226 | ||
| 22°C, Extruded at 380 to 390° F melt temperature 1 | 66.7 | J/cm | |
| 22°C, Extruded at 380 to 390° F melt temperature 2 | 178 | J/cm |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 71.7 | °C | ASTM D648 |
| CLTE - Flow (22°C) | 6.5E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | ASTM D635 |
| Note Message | |
|---|---|
| 1 . | Procedure A |
| 2 . | Procedure B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYLAN AF3500 | POLYMA Kunststoff GmbH & Co. KG | ABS | POLYLAN |
| RTP 4005 TFE 15 HB | RTP Company | PPA | RTP |
| Topilene® J800 | Hyosung Corporation | PP Homopolymer | Topilene® |
| Capilene® QT 80 A | Carmel Olefins Ltd. | PP Random Copolymer | Capilene® |
| Jackdaw PP EW16NT6686 | Jackdaw Polymers | PP, Unspecified | Jackdaw PP |