TOTAL Polyethylene HDPE BM 962
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polyethylene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gpTZUk_TOTAL-Polyethylene-HDPE-BM-962.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TOTAL Polyethylene BM 962 is a high density polyethylene material,. This product is available in North America or Asia Pacific region. The processing method is blow molding. The main features of the TOTAL Polyethylene BM 962 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.961 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 2.0 | g/10 min | ASTM D1238 |
| 190°C/21.6 kg | 55 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (10% Igepal) | 10.0 | hr | ASTM D1693B |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 29.6 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 500 | % | ASTM D638 |
| Flexural Modulus | 1310 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 290 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Melting Temperature | 129 | °C | ASTM D3418 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gardner Gloss (60°) | 25 | ASTM D523 |
| Additional Information |
|---|
| The value listed as Gloss, ASTM D523, was tested in accordance with Total internal methods.Elongation at Break, ASTM D638, Type IV, 2 in/min: >500%Gloss, ASTM D523, 60°: >25 |
| Note Message | |
|---|---|
| 1 . | Type 4, 51mm/min |
| 2 . | Type 4, 51mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Badamid® LB70 GF35 H | Bada AG | Nylon 6 | Badamid® |
| HiFill® PET GF30 2000 | Techmer Engineered Solutions | PET | HiFill® |
| POLIMAXX 2500H | IRPC Public Company Limited | PP Impact Copolymer | POLIMAXX |
| TECHNYL STAR® AFX 216 V60 GREY 2327 | Solvay Engineering Plastics | Nylon 66 | TECHNYL STAR® |
| Honghai CM 352L | Weifang Honghai Plastics Technology Co., Ltd. | CPE | Honghai |