TAROLOX 200 G2
| Category: | PBT+ASA , Polybutylene Terephthalate + ASA |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | TAROLOX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | goYmoS_TAROLOX-200-G2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PBT/ASA alloy 10% glass fibres reinforced. Good flow, excellent surface aspect, good combination of mechanical and thermal properties, good dimensional stability and low warpage behaviour. Preliminary Data Sheet. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.30 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 8.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | Internal method | ||
| Vertical flow direction | 0.60 - 0.90 | % | Internal method |
| Flow direction | 0.40 - 0.70 | % | Internal method |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 0.050 | % | ISO 62 |
| Saturated, 23°C | 0.25 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3900 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 65.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 4.8 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 3700 | MPa | ISO 178 |
| Flexural Stress 2 | 110 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.2 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C) | 45 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 3(1.8 MPa, Unannealed) | 145 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 150 | °C | ISO 306/B50 |
| Melting Temperature | 220 | °C | ISO 11357-3 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 650 | °C | IEC 60695-2-12 |
| Oxygen Index | 20 | % | ASTM D2863 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Reinforcement Content 4(750°C) | 10 | % | ISO 3451 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 240 - 260 | °C | |
| Mold Temperature | 80.0 - 110 | °C | |
| Injection Rate | Moderate-Fast |
| Injection instructions |
|---|
| Pre-heat Temperature: 120 to 130°CPre-heat Time: 3 hr |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| 2 . | 1.0 mm/min |
| 3 . | 120°C/hr |
| 4 . | 1 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultraform® FK 66003 | BASF Corporation | Acetal (POM) Copolymer | Ultraform® |
| Bapolan® 6409 | Bamberger Polymers, Inc. | PS (HIPS) | Bapolan® |
| LNP™ THERMOCOMP™ YF004 compound | SABIC Innovative Plastics | TPEE | LNP™ THERMOCOMP™ |
| LNP™ VERTON™ UX03320 compound | SABIC Innovative Plastics | PPA | LNP™ VERTON™ |
| Plaslube® J-1300/30/TF/15 | Techmer Engineered Solutions | PPS | Plaslube® |