Retpol® 3083 HS
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | PolyPacific Pty. Ltd. |
| Trademark: | Retpol® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | goLD9g_Retpol-3083-HS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Extron 3083 HS is a 50% glass fibre reinforced coupled polypropylene compound. It is a medium flow injection moulding grade developed for components requiring very high rigidity and excellent creep resistance with high heat deflection temperatures and good impact strength. It has been stabilized to meet automotive heat aging requirements of 21days at 150°C. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.35 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 0.10 to 0.40 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 3.00 mm) | 110 | ASTM D785 | |
| Durometer Hardness | ASTM D2240 | ||
| Shore D, 3.00 mm | 84 | ||
| Shore D, 15 sec, 3.00 mm | 80 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.00 mm) | 125 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.00 mm) | 2.0 | % | ASTM D638 |
| Flexural Modulus (3.00 mm) | 11000 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.00 mm) | 110 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.00 mm) | 680 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.00 mm | 160 | °C | |
| 1.8 MPa, Unannealed, 3.00 mm | 154 | °C | |
| CLTE - Flow (-30 to 30°C, 3.00 mm) | 3.0E-5 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Regrind | 10 | % | |
| Processing (Melt) Temp | 200 to 260 | °C | |
| Mold Temperature | 20.0 to 60.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Selvol™ E 305 | Sekisui Chemical Company, Ltd. | PVOH | Selvol™ |
| Tenopom® POM B3 MF NTLA010 PR303 | Petropol Industry and Trade of Polymers LTDA | Acetal (POM) Copolymer | Tenopom® POM |
| Cheng Yu ML1220 | Cheng Yu Plastic Company Limited | PC | Cheng Yu |
| FHR Polypropylene P5M6K-080 | Flint Hills Resources, LP | PP Random Copolymer | FHR Polypropylene |
| Karina RED PVC COMPOUND 902-42/291-IS (*) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |