TOTAL Polypropylene Lumicene® MR 2002
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polypropylene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | goIK2C_TOTAL-Polypropylene-Lumicene-MR-2002.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polypropylene Lumicene® MR 2002 is a metallocene homopolymer polypropylene with a Melt Flow Index 15 g/10 min for cast film. The specific design of the metallocene grade Lumicene® MR 2002 provides an exceptional processability on cast film lines. Films made of Lumicene® MR 2002 display an outstanding set of properties, combining exceptional optics with a toughness above conventional homopolymer based cast films. The extremely low extractable content is favorable for organoleptic properties. Polypropylene Lumicene® MR 2002 is characterized by high fluidity for high speed spinning on spun laid non-woven lines where spun filaments are produced to form a web that is then thermally bonded to manufacture products for hygienic and technical uses. Polypropylene Lumicene® MR 2002 has a special anti gas-fading formulation to reduce yellowing in fibres. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | ISO 1183 | ||
| -- 1 | 0.525 | g/cm³ | |
| -- | 0.905 | g/cm³ | |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 15 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 1300 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 50 µm, Cast Film | 24.0 | MPa | |
| TD : Yield, 50 µm, Cast Film | 23.0 | MPa | |
| MD : Break, 50 µm, Cast Film | 44.0 | MPa | |
| TD : Break, 50 µm, Cast Film | 33.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 50 µm, Cast Film | 550 | % | |
| TD : Break, 50 µm, Cast Film | 550 | % | |
| Dart Drop Impact (50 µm, Cast Film) | 320 | g | ISO 7765-1 |
| Elmendorf Tear Strength 2 | ISO 6383-2 | ||
| MD : 50.0 µm | 18.0 | kN/m | |
| TD : 50.0 µm | 19.0 | kN/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature (DSC) | 152 | °C | ISO 3146 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.0 µm, Cast Film) | 89 | ASTM D2457 | |
| Haze (50.0 µm, Cast Film) | 1.3 | % | ISO 14782 |
| Note Message | |
|---|---|
| 1 . | Bulk |
| 2 . | Cast Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SILVER® PA523M | Guangdong Silver Age Sci & Tech. Co., Ltd | Nylon 6 | SILVER® |
| Titanvene™ LL0209AA | PT. TITAN Petrokimia Nusantara | LLDPE | Titanvene™ |
| BESTPOLUX PCA85/01 | Triesa Plastics | PC+ABS | BESTPOLUX |
| HIPEX® HX8ICN (Series: HTR/OR) | KRAIBURG TPE | TPE | HIPEX® |
| Plexiglas® Resist zk4HC | Evonik Industries AG | Acrylic (PMMA) | Plexiglas® |