Sindustris PP R3421
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Sincerity Australia Pty Ltd. |
| Trademark: | Sindustris PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gnlWGD_Sindustris-PP-R3421.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sindustris PP R3421 is a Polypropylene material. It is available in Asia Pacific. Typical application of Sindustris PP R3421: Film |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 7.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 85 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 34.3 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | > 500 | % | ASTM D638 |
| Flexural Modulus | 932 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 44 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 90.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 138 | °C | ASTM D1525 3 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Santoprene™ 691-65W175 | ExxonMobil Chemical | TPV | Santoprene™ |
| Utomer UT518 | Shanghai Utomer Material Science Co., Ltd. | TPU-Polyester | Utomer |
| Globalprene® 3414 | Lee Chang Yung Chemical Industry Corp. | SBS | Globalprene® |
| EQUATE PE EFDC-7087 | EQUATE Petrochemical Company KSCC | LLDPE | EQUATE PE |
| HiFill® PEEK GF30 A NAT | Techmer Engineered Solutions | PEEK | HiFill® |