DURACON® SW-01
| Category: | Acetal (POM) Copolymer+PE , Acetal (POM) Copolymer + PE |
| Manufacturer: | Polyplastics Co., Ltd. |
| Trademark: | DURACON® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gngKzI_DURACON-SW-01.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High Sliding |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.42 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 7.0 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 6.00 | cm³/10min | ISO 1133 |
| Water Absorption (23°C, 24 hr) | 0.60 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 70 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2700 | MPa | ISO 527-2 |
| Tensile Stress | 50.0 | MPa | ISO 527-2 |
| Nominal Tensile Strain at Break | 20 | % | ISO 527-2 |
| Flexural Modulus | 2500 | MPa | ISO 178 |
| Flexural Stress | 75.0 | MPa | ISO 178 |
| Coefficient of Friction | JIS K7218 | ||
| Dynamic 1 | 0.21 | JIS K7218 | |
| With steel-dynamic 2 | 0.14 | JIS K7218 | |
| Wear Factor | JIS K7218 | ||
| 0.98 MPa, 0.30 m/sec 3 | < 1.0 | 10^-8 mm³/N·m | JIS K7218 |
| 0.98 MPa, 0.30 m/sec 4 | 16 | 10^-8 mm³/N·m | JIS K7218 |
| 0.060 MPa, 0.15 m/sec 5 | 400 | 10^-8 mm³/N·m | JIS K7218 |
| 0.060 MPa, 0.15 m/sec 6 | 900 | 10^-8 mm³/N·m | JIS K7218 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 5.4 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 80.0 | °C | ISO 75-2/A |
| Linear thermal expansion coefficient | Internal method | ||
| Flow : 23 to 55°C | 1.1E-4 | cm/cm/°C | Internal method |
| Lateral : 23 to 55°C | 1.1E-4 | cm/cm/°C | Internal method |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 2.0E+14 | ohms·cm | IEC 60093 |
| Dielectric Strength (3.00 mm) | 18 | kV/mm | IEC 60243-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Color Number | CF2001/CD3501 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 90.0 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Processing (Melt) Temp | 190 - 210 | °C | |
| Mold Temperature | 60.0 - 80.0 | °C | |
| Injection Pressure | 49.0 - 98.0 | MPa | |
| Screw Speed | 100 - 150 | rpm |
| Injection instructions |
|---|
| Injection speed: 5-50 mm/sInjection Holding pressure: Gate sealing time + alphaCooling: Plasticizing time or ejection capable time |
| Note Message | |
|---|---|
| 1 . | vs. M90-44, 0.06 MPa, 15 cm/s |
| 2 . | 0.98 MPa, 30 cm/s |
| 3 . | vs C-Steel, Steel Side |
| 4 . | vs C-Steel, Material Side |
| 5 . | vs M90-44, Material Side |
| 6 . | vs M90-44, M90-44 Side |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Yanshan PE LD361 | SINOPEC Beijing Yanshan Petrochemical | LDPE | Yanshan PE |
| NORYL GTX™ GTX673 resin | SABIC Innovative Plastics | PPE+PS+Nylon | NORYL GTX™ |
| DELPET™ 80NR-S | Asahi Kasei Chemicals Corporation | Acrylic (PMMA) | DELPET™ |
| LNP™ VERTON™ RVL29ESS compound | SABIC Innovative Plastics Europe | Nylon 66 | LNP™ VERTON™ |
| Starex VT-0826 | LOTTE ADVANCED MATERIALS CO., LTD. | ABS | Starex |