Skyrol® SH64
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | SKC Inc. |
| Trademark: | Skyrol® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gnEimP_Skyrol-SH64.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Skyrol ® SH64 is an optically clear film that has been pretreated on both sides. One side is pretreated for excellent performance in most print processes, and the other side is treated with an antistatic coating for write-on, wipe-off applications. SH64 has excellent processability in converting and sheeting operations. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 1.40 | g/cm³ | ASTM D1505 |
| Molding Shrinkage | Internal Method | ||
| Flow : 150°C, 30 min, 0.0570 mm | 1.6 | % | |
| Flow : 150°C, 30 min, 0.0660 mm | 1.5 | % | |
| Across Flow : 150°C, 30 min, 0.0570 mm | 0.70 | % | |
| Across Flow : 150°C, 30 min, 0.0660 mm | 0.60 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic 2 | 0.30 | ||
| vs. Itself - Dynamic 3 | 0.30 | ||
| vs. Itself - Static 4 | 0.30 | ||
| vs. Itself - Static 5 | 0.40 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 57 µm | 221 | MPa | |
| MD : Yield, 66 µm | 221 | MPa | |
| TD : Yield, 57 µm | 241 | MPa | |
| TD : Yield, 66 µm | 221 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 57 µm | 140 | % | |
| MD : Break, 66 µm | 140 | % | |
| TD : Break, 57 µm | 120 | % | |
| TD : Break, 66 µm | 120 | % |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gardner Gloss | ASTM D523 | ||
| 57.0 µm | 181 | ||
| 66.0 µm | 181 | ||
| Transmittance | ASTM D1003 | ||
| 57.0 µm | 90.0 | % | |
| 66.0 µm | 89.0 | % | |
| Haze | ASTM D1003 | ||
| 57.0 µm | 1.7 | % | |
| 66.0 µm | 1.9 | % |
| Note Message | |
|---|---|
| 1 . | 57 µm |
| 2 . | 57 µm |
| 3 . | 66 µm |
| 4 . | 66 µm |
| 5 . | 57 µm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Zhongfa PP ZF-UV2 | Yuyao Zhongfa Engineering Plastics Co. Ltd. | PP, Unspecified | Zhongfa |
| AcryliMax 301HP | S&E Specialty Polymers, LLC | ABS | AcryliMax |
| KRATON® D1184 K | Kraton Polymers LLC | SBS | KRATON® |
| Hostalen PP H5416 K | LyondellBasell Industries | PP Random Copolymer | Hostalen |
| LubriOne™ PC-20GF/15T FR BLACK | PolyOne Corporation | PC | LubriOne™ |