Optimum® 2000
| Category: | Copolyester , Copolyester |
| Manufacturer: | RAUH Polymers, Inc. |
| Trademark: | Optimum® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gn3VDw_Optimum-2000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Optimum®2000 is a copolyester product,. It can be processed by extrusion or injection molding and is available in North America. The main characteristics are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 100 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.50 - 0.80 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.18 mm) | 48.3 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.18 mm) | 500 | % | ASTM D638 |
| Flexural Modulus (3.18 mm) | 1720 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C, 3.18 mm | No Break | ASTM D256 | |
| 23°C, 3.18 mm | 1400 | J/m | ASTM D256 |
| Instrumented Dart Impact | 36.2 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 3.18 mm) | 65.6 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 76.7 - 82.2 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 204 - 216 | °C | |
| Middle Temperature | 204 - 227 | °C | |
| Front Temperature | 216 - 232 | °C | |
| Nozzle Temperature | 227 - 246 | °C | |
| Processing (Melt) Temp | 227 - 232 | °C | |
| Mold Temperature | 21.1 - 37.8 | °C | |
| Injection Pressure | 55.2 - 68.9 | MPa | |
| Injection Rate | Moderate | ||
| Holding Pressure | 41.4 - 55.2 | MPa | |
| Back Pressure | 0.00 - 2.76 | MPa |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 204 | °C |
| Extrusion instructions |
|---|
| Down Stack: Top: 185 to 200°F Middle: 165 to 185°F Bottom: 185 to 200°F Up Stack: Top: 185 to 200°F Middle: 175 to 190°F Bottom: 170 to 180°F |
| Note Message | |
|---|---|
| 1 . | Type 1 |
| 2 . | Type 1 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VINIKA® CF80EA | Mitsubishi Chemical Performance Polymers, Inc. | PVC, Flexible | VINIKA® |
| Network Polymers PP PPB 25 0216 | Network Polymers, Inc. | PP Copolymer | Network Polymers PP |
| New-prene™ 6040B | Total Polymer Vision (Suzhou) Co., LTD | PP+EPDM | New-prene™ |
| Boda BDF331P | Chenguang Fluoro & Silicone Elastomers Co., Ltd. | Fluorelastomer | Boda |
| Hydroxy-Purge 30C | InChem Corp. | TP, Unspecified | Hydroxy-Purge |