Hostacom M2 U08 100000
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hostacom |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gn3LCR_HostacomM2U08100000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Hostacom M2 U08 100000 is a 20% talc filled PP homopolymer, with good flowability. Product is available as a customized color matched, pellet form. This grade is delivered in Black color version. This grade is not intended for medical, pharmaceutical, food and drinking water applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.05 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 12 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 13.0 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 39.0 | MPa | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 38 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 120 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 66.0 | °C | ISO 75-2/A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP ESD C 2800-65A | RTP Company | TPO (POE) | RTP |
| 4DUR® 9K22130 XHFR1 | 4Plas | PBT | 4DUR® |
| Nypol® PA A3 TZ PRTA010 NR355 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Exact™ 4151 | ExxonMobil Chemical | Plastomer | Exact™ |
| MAJORIS CFR269 - 1333 | AD majoris | PP, Unspecified | MAJORIS |