SCHULAMID® 66 GF 33 FC
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gmhYLB_SCHULAMID66GF33FC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 33% glassfiber reinforced PA 66 for food contact applications |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.39 | -- | g/cm³ | ISO 1183/A |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 11000 | 8000 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 170 | 125 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 2.5 | 4.7 | % | ISO 527-2/1A/5 |
| Flexural Modulus 1 | 9200 | -- | MPa | ISO 178 |
| Flexural Stress 2(3.5% Strain) | 178 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 7.0 | -- | kJ/m² | ISO 179/1eA |
| 23°C | 9.0 | 12 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 60 | -- | kJ/m² | ISO 179/1eU |
| 23°C | 65 | 75 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | > 250 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 239 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | > 250 | -- | °C | ISO 306/A50, ISO 306/B50 |
| Ball Pressure Test (185°C) | Pass | -- | IEC 60695-10-2 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 0.8 mm | HB | -- | IEC 60695-11-10, -20 | |
| 1.6 mm | HB | -- | IEC 60695-11-10, -20 | |
| 3.2 mm | HB | -- | IEC 60695-11-10, -20 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 1.5 mm | 650 | -- | °C | IEC 60695-2-12 |
| 3.0 mm | 675 | -- | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
| 1.5 mm | 675 | -- | °C | IEC 60695-2-13 |
| 3.0 mm | 700 | -- | °C | IEC 60695-2-13 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.040 - 0.10 | % | |
| Suggested Max Regrind | 20 | % | |
| Processing (Melt) Temp | 280 - 300 | °C | |
| Mold Temperature | 60 - 120 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen RP348N | PolyMirae | PP Random Copolymer | Moplen |
| TROGAMID® T BX7304 | Evonik Industries AG | Nylon 6/3T | TROGAMID® T |
| Advanced Composites ATX781 | Advanced Composites, Inc. | PP, Unspecified | Advanced Composites |
| Petlon Prime A2-G15-00-NT | Petlon Polymers Ltd | Nylon 6 | Petlon Prime |
| Celstran® PBT-CF40-08 | Celanese Corporation | PBT | Celstran® |