Rilsan® BECV0 P40 TL
| Category: | Nylon 11 , Polyamide 11 |
| Manufacturer: | Arkema |
| Trademark: | Rilsan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gmhHfI_Rilsan-BECV0-P40-TL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Rilsan® BECV0 P40 TL is a Polyamide 11 (Nylon 11) product. It can be processed by extrusion and is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Water Absorption | ASTM D570 | ||
| 24 hr | 0.30 | % | |
| Saturation | 1.0 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 78 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 63.4 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 360 | % | ASTM D638 |
| Flexural Modulus | 310 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C | 16 | J/m | |
| 23°C | 430 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 41.1 | °C | ASTM D648 |
| Melting Temperature | 186 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shuman ABS/PC 380 | Shuman Plastics, Inc. | PC+ABS | Shuman ABS/PC |
| Nanjing Hongrui PC C1000 | Nanjing Hongrui Engineering Plastics Co., Ltd. | PC | Nanjing Hongrui PC |
| Bergamid™ B700 W25 | PolyOne Corporation | Nylon 6 | Bergamid™ |
| Clariant Nylon 6/6 PA-131G33 | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| DURANEX® 700FP | Polyplastics Co., Ltd. | PBT | DURANEX® |