LUVOCOM® 1800-8609 Datasheet,PET,LEHVOSS Group-SHANGHAI SUSHENG

Message
LUVOCOM®1800-8609 is a polyethylene terephthalate (PET) material, which contains a glass fiber reinforced material. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,. LUVOCOM®The main features of 1800-8609 are: Good stiffness Wear-resistant Lubrication Typical application areas include: engineering/industrial accessories textile/fiber Automotive Industry business/office supplies

General Information
Filler / Reinforcement	Glass fiber reinforced material
Additive	PTFE lubricant
Features	Low friction coefficient Rigid, good Good strength Good wear resistance Lubrication
Uses	Gear Textile applications Engineering accessories Application in Automobile Field Business equipment Cam Bearing
Appearance	Natural color

Physical	Nominal Value	Unit	Test Method
Density	1.85	g/cm³	ISO 1183
Molding Shrinkage	0.10 - 0.40	%	DIN 16901
Water Absorption (23°C, 24 hr)	< 0.30	%

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	15000	MPa	ISO 527-2
Tensile Stress (Break)	160	MPa	ISO 527-2
Tensile Strain (Yield)	2.0	%	ISO 527-2
Flexural Modulus	13000	MPa	ISO 178
Flexural Stress	230	MPa	ISO 178
Flexural Strain at Flexural Strength	2.6	%	ISO 178

Thermal	Nominal Value	Unit	Test Method
Maximum operating temperature- Short Term	180	°C

Electrical	Nominal Value	Unit	Test Method
Insulation Resistance	> 1.0E+12	ohms	IEC 60167

Impact	Nominal Value	Unit	Test Method
Charpy Unnotched Impact Strength (23°C)	55	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Continuous Use Temperature	110	°C	UL 746B

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	> 1.0E+12	ohms	IEC 60093

Injection	Nominal Value	Unit
Drying Temperature
Hot air dryer	120	°C
Hot air dryer, B	80	°C
Drying Time
Hot air dryer	2.0 - 5.0	hr
Hot air dryer, B	6.0 - 8.0	hr
Rear Temperature	285 - 295	°C
Middle Temperature	270 - 280	°C
Front Temperature	265 - 275	°C
Nozzle Temperature	265 - 275	°C
Processing (Melt) Temp	280	°C
Mold Temperature	60 - 120	°C

Injection instructions
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.02%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. As the material absorbs water very quickly, the predried material should be fed to the processing immediately. Processing temperatures above 300°C may very rapidly cause thermal damage and should therefore be avoided. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Injection instructions

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.02%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. As the material absorbs water very quickly, the predried material should be fed to the processing immediately. Processing temperatures above 300°C may very rapidly cause thermal damage and should therefore be avoided. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Category:	PET , Polyethylene Terephthalate
Manufacturer:	LEHVOSS Group
Trademark:	LUVOCOM®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	gmaFH0_LUVOCOM18008609.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
RTP 300 TFE 5	RTP Company	PC	RTP
TAIRIPRO K1023	Formosa Plastics Corporation	PP Homopolymer	TAIRIPRO
WeatherPro™ Centrex®/ABS SP-6710	Spartech Plastics	ASA+AES	WeatherPro™
Generic PPE+PS - Mineral	Generic	PPE+PS	Generic
Hylox® 9000	Ravago Manufacturing Americas, LLC	PBT	Hylox®