Celanex® 3300FC
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Celanese Corporation |
| Trademark: | Celanex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gm6zFI_Celanex-3300FC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Celanex 3300FC is a general purpose, 30% glass reinforced, polybutylene terephthalate that offers a superior combination of mechanical, electrical, and thermal properties. This grade provides outstanding processability and good chemical resistance. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.53 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | 16 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (250°C/2.16 kg) | 17.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Flow | 0.30 - 0.50 | % | ASTM D955 |
| Vertical flow direction | 0.70 - 1.1 | % | ISO 294-4 |
| Flow direction | 0.30 - 0.70 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.20 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 90 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -40°C | 11000 | MPa | ASTM D638 |
| 0°C | 10500 | MPa | ASTM D638 |
| 23°C | 9650 | MPa | ASTM D638 |
| 80°C | 4830 | MPa | ASTM D638 |
| 121°C | 3760 | MPa | ASTM D638 |
| -- | 9200 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Fracture, -40°C | 190 | MPa | ASTM D638 |
| Fracture, 0°C | 159 | MPa | ASTM D638 |
| Fracture, 23°C | 134 | MPa | ASTM D638 |
| Fracture, 80°C | 77.2 | MPa | ASTM D638 |
| Fracture, 121°C | 61.4 | MPa | ASTM D638 |
| Fracture | 130 | MPa | ISO 527-2/1A/5 |
| Tensile Elongation | |||
| Fracture, -40°C | 1.9 | % | ASTM D638 |
| Fracture, 0°C | 1.9 | % | ASTM D638 |
| Fracture, 23°C | 2.0 | % | ASTM D638 |
| Fracture, 80°C | 3.9 | % | ASTM D638 |
| Fracture, 121°C | 4.3 | % | ASTM D638 |
| Fracture | 2.5 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 9700 | MPa | ISO 178 |
| Flexural Stress (23°C) | 210 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 8.5 | kJ/m² | ISO 179/1eA |
| 23°C | 8.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 45 | kJ/m² | ISO 179/1eU |
| 23°C | 46 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 7.5 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 225 | °C | ISO 75-2/B |
| 0.45 MPa, annealed | 228 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 206 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 205 | °C | ISO 75-2/A |
| 8.0 MPa, not annealed | 150 | °C | ISO 75-2/C |
| Glass Transition Temperature 1 | 60.0 | °C | ISO 11357-2 |
| Vicat Softening Temperature | 220 | °C | ISO 306/B50 |
| Melting Temperature 2 | 225 | °C | ISO 11357-3, ASTM D3418 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 2.5E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 1.0E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | |||
| -- | 1.0E+15 | ohms·cm | ASTM D257 |
| -- | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | |||
| -- 3 | 22 | kV/mm | ASTM D149 |
| -- | 31 | kV/mm | IEC 60243-1 |
| Dielectric Constant | |||
| 1 MHz | 3.70 | ASTM D150 | |
| 100 Hz | 4.50 | IEC 60250 | |
| 1 MHz | 4.10 | IEC 60250 | |
| Dissipation Factor | |||
| 1 MHz | 2.0E-3 | ASTM D150 | |
| 100 Hz | 2.2E-3 | IEC 60250 | |
| 1 MHz | 0.016 | IEC 60250 | |
| Comparative Tracking Index | 425 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.710 mm) | HB | UL 94 | |
| Oxygen Index | 20 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 130 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 20.0 - 50.0 | °C | |
| Rear Temperature | 230 - 240 | °C | |
| Middle Temperature | 235 - 250 | °C | |
| Front Temperature | 235 - 250 | °C | |
| Nozzle Temperature | 250 - 260 | °C | |
| Processing (Melt) Temp | 235 - 260 | °C | |
| Mold Temperature | 65.0 - 93.0 | °C | |
| Injection Rate | Moderate-Fast |
| Injection instructions |
|---|
| Manifold Temperature: 250 to 260°CZone 4 Temperature: 240 to 260°CFeed Temperature: 230 to 240°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 10°C/min |
| 3 . | Method A (short time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 506 FR | RTP Company | SAN | RTP |
| Shandong PA1010 PA1010 | Shandong Dongchen Engineering Plastics Co., Ltd. | Nylon 1010 | Shandong PA1010 |
| UBE Nylon 1018I | UBE Industries, Ltd. | Nylon 6 | UBE Nylon |
| PALSAFE® R 15 | pal plast GmbH | PC | PALSAFE® |
| NORYL GTX™ GTX678 resin | SABIC Innovative Plastics | PPE+PS+Nylon | NORYL GTX™ |