TRIBOCOMP® PA66 GF30 TS13
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | EPIC Polymers |
| Trademark: | TRIBOCOMP® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gm00v2_TRIBOCOMP-PA66-GF30-TS13.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TRIBOCOMP® PA66 GF30 TS13 is a Polyamide 66 (Nylon 66) product filled with 30% glass fiber. It is available in Europe. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.34 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.40 | -- | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.6 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 9400 | 6800 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 175 | 125 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 3.0 | 6.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 8100 | 5600 | MPa | ISO 178 |
| Flexural Stress (23°C) | 250 | 185 | MPa | ISO 178 |
| Coefficient of Friction 1 | ASTM D3702 | |||
| vs. Itself - Dynamic | 0.19 | -- | ||
| vs. Itself - Static | 0.16 | -- | ||
| Wear Factor (23°C) | 18.0 | -- | ASTM D3702 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 11 | -- | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 70 | -- | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 250 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 250 | -- | °C | ISO 75-2/A |
| CLTE - Flow (23°C) | 3.0E-5 | -- | cm/cm/°C | ISO 7991 |
| Thermal Conductivity | 0.28 | -- | W/m/K | ISO 22007 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | -- | ohms | ASTM D257 |
| Electric Strength | 36 | 32 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 500 | 500 | V | IEC 60112 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 270 to 300 | °C | |
| Middle Temperature | 275 to 295 | °C | |
| Front Temperature | 280 to 295 | °C | |
| Nozzle Temperature | 290 to 310 | °C | |
| Processing (Melt) Temp | < 300 | °C | |
| Mold Temperature | 80.0 to 130 | °C |
| Note Message | |
|---|---|
| 1 . | 23°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ShinkoLite-P MF | Mitsubishi Rayon America Inc. | Acrylic (PMMA) | ShinkoLite-P |
| Mylar® A (1400 guage) | DuPont Teijin Films U.S. | PET | Mylar® |
| Infino NE-1010 | SAMSUNG SDI CO., LTD. | PC+ABS | Infino |
| PENTAMID B GV40 H natur | PENTAC Polymer GmbH | Nylon 6 | PENTAMID B |
| Rigidex® HD5760UA | INEOS Olefins & Polymers Europe | HDPE Copolymer | Rigidex® |