LONGLITE® PMC T 33
| Category: | Phenolic , Phenolic |
| Manufacturer: | CCP Group |
| Trademark: | LONGLITE® PMC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gllO6K_LONGLITE-PMC-T-33.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PMC T 33 is a granular wood flour and mineral reinforced phenolic product for compression moulding |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.37 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | 0.80 | % | JIS K6915 |
| Water Absorption | |||
| 24 hr | 0.50 | % | ASTM D570 |
| 23°C, 24 hr | 0.50 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | |||
| Yield | 55.0 | MPa | ISO 527-2 |
| -- | 55.0 | MPa | ASTM D638 |
| Flexural Strength | 75.0 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (6.35 mm) | 23 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 155 | °C | ASTM D648, ISO 75-2/A |
| Melting Temperature 1 | 170 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+10 | ohms | ASTM D257, IEC 60093 |
| Volume Resistivity | 1.0E+12 | ohms·cm | ASTM D257, IEC 60093 |
| Dielectric Strength (2.00 mm) | 10 | kV/mm | ASTM D149, IEC 60243-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (6.35 mm) | V-0 | UL 94 |
| Additional Information |
|---|
| Monohole, CCP: 18 GDensity, ASTM D792 & ISO 1183: 1.36 to 1.37 g/cm³Charpy Notched Impact Strength, ASTM D256: 2.7 kg cm/cm²Compression Molding Conditions -Preheating Temperature: 90 to 120°CMold Temperature: 150 to 180°CMolding Presssure: 150 to 1000 bar |
| Note Message | |
|---|---|
| 1 . | Maximum application, 2 hours |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Thermoplastic Polyolefin FT2600-01UV | RheTech, Inc. | Polyolefin, Unspecified | RheTech Thermoplastic Polyolefin |
| NYCOA Polyamide 715 C | Nycoa (Nylon Corporation of America) | Nylon 6 | NYCOA Polyamide |
| Artenius XCEL L | Artenius | PETG | Artenius |
| Sylvin 4200-70 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| MARPOL® FSB | Marco Polo International, Inc. | PS (EPS) | MARPOL® |