| 4LEX 25F10000 is a MFI 10 to 15 Unfilled Polycarbonate |
| General Information | |
|---|---|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.24 | g/cm³ | ISO 1183 |
| Water Absorption 1(Equilibrium, 23°C, 50% RH) | 0.15 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2350 | MPa | ISO 527-2/5 |
| Tensile Stress (Break, 23°C) | 52.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 93 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180/1A | ||
| -30°C | 15 | kJ/m² | ISO 180/1A |
| 23°C | 60 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 144 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 145 | °C | ISO 306/B |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index | 200 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 870 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 260 - 300 | °C | |
| Mold Temperature | 80.0 - 100 | °C | |
| Injection Rate | Moderate-Fast | ||
| Holding Pressure | 60.0 - 120 | MPa | |
| Screw Speed | 200 | rpm |
| Injection instructions |
|---|
| Feed Throat Temperature: 60 - 80 °CBack Pressure: Low |
| Note Message | |
|---|---|
| 1 . | 24 Hrs |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen PP200P | LyondellBasell Industries | PP Random Copolymer | Moplen |
| Fainplast PVC PH 70/AS | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| Kumho ABS HU650 | Korea Kumho Petrochemical Co., Ltd. | ABS | Kumho ABS |
| POLLITE 1001C | POLYROCKS CHEMICAL CO., LTD | PC | POLLITE |
| TECACOMP® PA66 CF20 black 3708 | Ensinger GmbH | Nylon 66 | TECACOMP® |