RTP 2099 X 121249 B
| Category: | PLA , Polylactic Acid |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gkO9r0_RTP-2099-X-121249-B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Standard Nucleator - Glass Fiber - 78% Renewable Resource Content |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.39 | g/cm³ | ASTM D792 |
| Moisture Content | 0.020 | % |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Primary Additive | 20 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8270 | MPa | ASTM D638 |
| Tensile Strength | 96.5 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 1.5 | % | ASTM D638 |
| Flexural Modulus | 8620 | MPa | ASTM D790 |
| Flexural Strength | 117 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 48 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 320 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 152 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 148 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 54.4 | °C | |
| Drying Time | 2.0 - 6.0 | hr | |
| Dew Point | -40.0 | °C | |
| Processing (Melt) Temp | 171 - 193 | °C | |
| Mold Temperature | 82.2 - 104 | °C | |
| Injection Pressure | 55.2 - 103 | MPa |
| Injection instructions |
|---|
| Desiccant Type Dryer Required. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYLAN T-100FW | POLYMA Kunststoff GmbH & Co. KG | ABS | POLYLAN |
| Reny® 1002H | Mitsubishi Engineering-Plastics Corp | PARA | Reny® |
| Double Elephant SX-304 | Suzhou Double Elephant Optical Material Co., LTD. | Acrylic (PMMA) | Double Elephant |
| Edgetek™ X TR2-20TA/000 NATURAL | PolyOne Corporation | Copolyester | Edgetek™ |
| LEXAN™ FST3403 resin | SABIC Innovative Plastics | PC | LEXAN™ |