LG PS 25SP(E)
| Category: | PS (GPPS) , General Purpose Polystyrene |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | LG PS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | giBHX1_LG-PS-25SP-E-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LG PS 25SP(E) is a general-purpose polystyrene material,. This product is available in North America, Latin America, Europe or Asia Pacific. The processing method is injection molding. The main features of LG PS 25SP(E) are:
Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 200°C/5.0 kg | 3.0 | g/10 min | ASTM D1238 |
| 220°C/10.0 kg | 39 | g/10 min | ASTM D1238 |
| 230°C/3.8 kg | 8.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 - 0.80 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 121 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1(3.20 mm) | 2880 | MPa | ASTM D638 |
| Tensile Strength 2(Yield, 3.20 mm) | 52.0 | MPa | ASTM D638 |
| Tensile Elongation 3(Break, 3.20 mm) | 4.0 | % | ASTM D638 |
| Flexural Modulus 4(3.20 mm) | 3270 | MPa | ASTM D790 |
| Flexural Strength 5(Yield, 3.20 mm) | 98.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 6.40 mm | 9.8 | J/m | ASTM D256 |
| 23°C, 6.40 mm | 9.8 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm | 95.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 88.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 96.0 | °C | ASTM D1525 6 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | UL 94 | |
| 3.20 mm | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 170 - 190 | °C | |
| Middle Temperature | 180 - 200 | °C | |
| Front Temperature | 190 - 210 | °C | |
| Nozzle Temperature | 190 - 220 | °C | |
| Processing (Melt) Temp | 190 - 220 | °C | |
| Mold Temperature | 40.0 - 70.0 | °C | |
| Back Pressure | 29.4 - 58.8 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Injection instructions |
|---|
| Minimum Moisture Content: 0.01% |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 15 mm/min |
| 5 . | 15 mm/min |
| 6 . | 速率 A (50°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Stanyl® TW371 | DSM Engineering Plastics | Nylon 46 | Stanyl® |
| TAROMID B 280 Z2 G6 | Taro Plast S.p.A. | Nylon 6 | TAROMID B |
| Borclear™ RB707CF | Borealis AG | PP Random Copolymer | Borclear™ |