Borealis PP BC545MO
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | Borealis AG |
| Trademark: | Borealis PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ghVOyL_Borealis-PP-BC545MO.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
BC545MO is a low-blush polypropylene heterophasic copolymer intended for injection moulding. This grade features high impact strength, high thermal stability and very good processability. As all polypropylenes, this grade shows excellent stress-cracking and chemical resistances. This grade is characterized by combination of high stiffness, very high impact strength and low stress whitening. This grade is mildly nucleated to maximize the stiffness-impact balance. The additive formulation provides longterm heat stability. Its very good organoleptic properties allows this grade to be used with any masterbatch without discoloring problems. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.908 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.5 | g/10 min | ISO 1133 |
| Molding Shrinkage | 1.5 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Injection Molded) | 1250 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, Injection Molded) | 25.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield, Injection Molded) | 8.0 | % | ISO 527-2/50 |
| Flexural Modulus 1(Injection Molded) | 1200 | MPa | ISO 178 |
| Flexural Stress (Injection Molded) | 30.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C, Injection Molded | 6.0 | kJ/m² | |
| 23°C, Injection Molded | 12 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -20°C, Injection Molded | 5.5 | kJ/m² | |
| 23°C, Injection Molded | 11 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 2 | |||
| 0.45 MPa, Unannealed | 90.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 54.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 150 | °C | ISO 306/A |
| -- | 70.0 | °C | ISO 306/B |
| Melt Energy | 110 | kJ/kg | ISO 11357 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 230 to 260 | °C | |
| Mold Temperature | 10.0 to 30.0 | °C | |
| Injection Rate | Fast | ||
| Holding Pressure | 20.0 to 50.0 | MPa |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | Injection molded |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RMA 62 | Ronald Mark Associates, Inc. | PVC Homopolymer | RMA |
| Eltex® P KS309 | INEOS Olefins & Polymers Europe | PP Random Copolymer | Eltex® P |
| Jampilen HP421H | Jam Polypropylene Company | PP Homopolymer | Jampilen |
| Ultramid® A3WG10 CR BK00564 | BASF Corporation | Nylon 66 | Ultramid® |
| Rotuba CAB B9024 (11% Plasticizer) | Rotuba Extruders, Inc. | CAB | Rotuba CAB |