| Category: | PUR, Unspecified , Polyurethane |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ggI6Kr_Generic-PUR-Unspecified.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PUR, Unspecified This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.869 - 1.42 | g/cm³ | ASTM D792 |
| 23°C | 0.920 - 1.25 | g/cm³ | ISO 1183 |
| -- | 0.160 - 1.39 | g/cm³ | ASTM D1505 |
| Apparent Density | 0.94 - 1.11 | g/cm³ | ASTM D1895 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.010 - 1.3 | % | ASTM D955 |
| 23°C | 0.30 - 1.8 | % | ISO 294-4 |
| Water Absorption | ASTM D570 | ||
| 23°C, 24 hr | 0.030 - 0.46 | % | ASTM D570 |
| Saturated, 23°C | 0.37 - 0.50 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | |||
| 23°C | 49 - 91 | ASTM D2240 | |
| 23°C | 29 - 94 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 4.83 - 2190 | MPa | ASTM D638 |
| Tensile Strength | |||
| Yield, 23°C | 0.0758 - 48.0 | MPa | ASTM D638 |
| Yield, 23°C | 15.9 - 45.3 | MPa | ISO 527-2 |
| Fracture, 23°C | 16.8 - 62.1 | MPa | ASTM D638 |
| Fracture, 23°C | 8.69 - 25.5 | MPa | ISO 527-2 |
| 23°C | 5.49 - 53.8 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield, 23°C | 3.3 - 78 | % | ASTM D638 |
| Fracture, 23°C | 0.40 - 17 | % | ASTM D638 |
| Fracture, 23°C | 3.0 - 130 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 37.9 - 2690 | MPa | ASTM D790 |
| 23°C | 107 - 3370 | MPa | ISO 178 |
| Flexural Strength | ASTM D790 | ||
| 23°C | 2.00 - 81.4 | MPa | ASTM D790 |
| Yield, 23°C | 12.4 - 108 | MPa | ASTM D790 |
| Compressive Modulus | 222 - 2480 | MPa | ASTM D695 |
| Compressive Strength (23°C) | 1.24 - 71.9 | MPa | ASTM D695 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% strain, 23°C | 0.172 - 5.83 | MPa | ASTM D412 |
| 200% strain, 23°C | 1.38 - 2.12 | MPa | ASTM D412 |
| 300% strain, 23°C | 1.97 - 6.95 | MPa | ASTM D412 |
| Tensile Strength | ASTM D412 | ||
| Yield, 23°C | 2.07 - 66.0 | MPa | ASTM D412 |
| Fracture, 23°C | 1.38 - 6.34 | MPa | ASTM D412 |
| Tensile Elongation | ASTM D412 | ||
| Yield | 320 - 800 | % | ASTM D412 |
| Fracture, 23°C | 2.0 - 1000 | % | ASTM D412 |
| Tear Strength (23°C) | 2.14 - 83.1 | kN/m | ASTM D624 |
| Compression Set | 5.0 - 67 | % | ASTM D395 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 9.6 - 95 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 23 - 1600 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 51.9 - 107 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 46.3 - 95.8 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 35.0 - 140 | °C | ISO 75-2/A |
| Continuous Use Temperature | 48.9 - 131 | °C | ASTM D794 |
| Glass Transition Temperature | -63.0 - 106 | °C | ASTM E1356 |
| CLTE - Flow | 4.0E-5 - 3.8E-4 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | |||
| 23°C | 0.037 - 0.35 | W/m/K | ASTM C177 |
| 23°C | 0.20 - 0.21 | W/m/K | ISO 8302 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 4.0 - 1.7E+16 | ohms | ASTM D257 |
| Volume Resistivity | |||
| 23°C | 5.2E+6 - 1.5E+15 | ohms·cm | ASTM D257 |
| 23°C | 3.8E+9 - 1.1E+14 | ohms·cm | IEC 60093 |
| Dielectric Strength | |||
| 23°C | 11 - 28 | kV/mm | ASTM D149 |
| 23°C | 19 - 36 | kV/mm | IEC 60243-1 |
| Dielectric Constant | |||
| 23°C | 2.69 - 5.82 | ASTM D150 | |
| 23°C | 3.26 - 3.95 | ASTM D2520 | |
| 23°C | 3.00 - 6.14 | IEC 60250 | |
| Dissipation Factor (23°C) | 3.0E-4 - 0.045 | ASTM D150 | |
| Arc Resistance | 120 - 122 | sec | ASTM D495 |
| Insulation Resistance (23°C) | 1.0E+11 - 2.6E+13 | ohms | IEC 60167 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Pot Life (23°C) | 0.033 - 41 | min | |
| Shelf Life (23°C) | 24 - 78 | wk | |
| Thermoset Mix Viscosity | 25.0 - 15000 | cP | ASTM D2393 |
| Demold Time | 4.5 - 10000 | min | |
| Post Cure Time | 0.42 - 180 | hr |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (22.8°C) | 470 - 3300 | mPa·s | ASTM D3236 |
| Melt Viscosity | 0.0700 - 104 | Pa·s | ASTM D3835 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 65.6 - 107 | °C | |
| Drying Time | 2.0 - 5.0 | hr | |
| Processing (Melt) Temp | 193 - 232 | °C | |
| Mold Temperature | 27.2 - 73.9 | °C |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PUR, UnspecifiedThis information is provided for comparative purposes only. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 76.7 - 216 | °C | |
| Cylinder Zone 2 Temp. | 85.0 - 224 | °C | |
| Cylinder Zone 3 Temp. | 87.8 - 232 | °C | |
| Melt Temperature | 79.4 - 238 | °C | |
| Die Temperature | 79.4 - 238 | °C |
| Extrusion instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PUR, UnspecifiedThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PPcompound 15T1040 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |
| Novamid® ES110C | DSM Engineering Plastics | Nylon 6 | Novamid® |
| Flexoprene® 95 | Puma Tecnica S.A.I.C.F.I | PE, Unspecified | Flexoprene® |
| LNP™ STAT-LOY™ 63000CT compound | SABIC Innovative Plastics Asia Pacific | PC+Polyester | LNP™ STAT-LOY™ |
| Polyrocks EP8400X105V-1 | Polyrocks Chemical Co., Ltd | XLPE | Polyrocks |