Hostacom 75F4-2
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hostacom |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ggGxLu_Hostacom-75F4-2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Hostacom 75F4-2 conventional melt flow, 1,700 MPa flexural modulus, 20% talc-filled polypropylene copolymer has an excellent combination of strength, stiffness, impact resistance and colorability. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 4.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (23°C, 48 hr, 3.20 mm) | 1.2 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 86 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 26.0 | MPa | |
| Break | 17.0 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield | 7.0 | % | |
| Break | 150 | % | |
| Flexural Modulus - Tangent 1 | 1700 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 53 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 100 | °C | ASTM D648 |
| Note Message | |
|---|---|
| 1 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WINDFORM® XT 2.0 | CRP Technology s.r.l. | Nylon, Unspecified | WINDFORM® |
| UmaPET MO | Ester Industries Ltd. | PET | UmaPET |
| Generic PP Homopolymer - Talc | Generic | PP Homopolymer | Generic |
| THERMORUN® Z103B/N | Mitsubishi Chemical Performance Polymers, Inc. | TPE | THERMORUN® |
| OTECH TPE OW128W - Cable Jacket | OTECH Corporation | TPE | OTECH TPE |