LOFEX® A3110
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | Lotte Chemical Corporation |
| Trademark: | LOFEX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gg10g6_LOFEX-A3110.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LOFEX ® A3110 Polyester film is optically clear and one side corona treated with excellent properties by tensile strength , proper elongation and the thermal contraction rate. It can use by advertisement material because it has excellent run, easy treatment by suitable product. Also, it is a product that thickness control is possible according to customer needs. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Surface Tension | |||
| 100.0 µm | 52 | mN/m | |
| 175.0 µm | 52 | mN/m |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| F5 | ASTM D882 | ||
| MD : 100.0 µm | 113 | MPa | |
| MD : 175.0 µm | 108 | MPa | |
| TD : 100.0 µm | 113 | MPa | |
| TD : 175.0 µm | 108 | MPa |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Shrinkage | Internal Method | ||
| MD, 30 min : 150°C, 100.0 µm | 1.0 | % | |
| MD, 30 min : 150°C, 175.0 µm | 1.0 | % | |
| TD, 30 min : 150°C, 100.0 µm | 0.50 | % | |
| TD, 30 min : 150°C, 175.0 µm | 0.50 | % | |
| Surface Treatment | Inside (Corona) |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic | 0.29 | ||
| vs. Itself - Static | 0.32 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 100 µm | 196 | MPa | |
| MD : Yield, 180 µm | 196 | MPa | |
| TD : Yield, 100 µm | 216 | MPa | |
| TD : Yield, 180 µm | 206 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 100 µm | 170 | % | |
| MD : Break, 180 µm | 170 | % | |
| TD : Break, 100 µm | 120 | % | |
| TD : Break, 180 µm | 130 | % |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gardner Gloss | ASTM D523 | ||
| 60°, 100 µm | 175 | ||
| 60°, 175 µm | 175 | ||
| Transmittance | ASTM D1003 | ||
| 100 µm | 89.0 | % | |
| 175 µm | 89.0 | % | |
| Haze | ASTM D1003 | ||
| 100 µm | 2.1 | % | |
| 175 µm | 2.7 | % |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Xuchuan XCS-3995 | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| DynaMix™ 2044-GBD | Polymer Dynamix | Nylon, Unspecified | DynaMix™ |
| Electrafil® J-3/CF/30 | Techmer Engineered Solutions | Nylon 6 | Electrafil® |
| Jampilen HP501D | Jam Polypropylene Company | PP Homopolymer | Jampilen |
| ALTECH® NXT PP-H A 2030/456 LE GF30 CP | ALBIS PLASTIC GmbH | PP Homopolymer | ALTECH® NXT PP-H |