Order Products : sales@su-jiao.com
TAIRILAC AT5500
| Category: | MABS , Methyl Methacrylate / ABS |
| Manufacturer: | Formosa Plastics Corporation |
| Trademark: | TAIRILAC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gfYc3R_TAIRILAC-AT5500.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| FCFC ABS resin AT5500 meets the requirements of UL, SGS and the certificates of environmental protection. |
| General Information | |
|---|---|
| Agency Ratings |
|
| RoHS Compliance |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.07 | g/cm³ | ASTM D792 |
| 23°C | 1.07 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238, ISO 1133 | ||
| 200°C/5.0 kg | 2.2 | g/10 min | ASTM D1238, ISO 1133 |
| 220°C/10.0 kg | 22 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage - Flow | 0.40 - 0.70 | % | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class R, 23°C | 103 | ASTM D785 | |
| R scale, 23°C | 103 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| 23°C | 41.2 | MPa | ASTM D638 |
| 23°C | 41.0 | MPa | ISO 527-2 |
| Flexural Modulus (23°C) | 2160 | MPa | ASTM D790, ISO 178 |
| Flexural Strength (23°C) | 70.0 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact (23°C, 6.35 mm) | 140 | J/m | ISO 180, ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648, ISO 75-2/A | ||
| 1.8 MPa, unannealed, 12.7mm | 86.0 | °C | ASTM D648, ISO 75-2/A |
| 1.8 MPa, annealed 1 | 96.0 | °C | ASTM D648, ISO 75-2/A |
| Vicat Softening Temperature | 102 | °C | ISO 306/A, ASTM D1525 2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, All Colors) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 80.0 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Mold Temperature | 40.0 - 80.0 | °C | |
| Injection Pressure | 68.6 - 108 | MPa |
| Injection instructions |
|---|
| Screw Temp: 190 to 230°C |
| Note Message | |
|---|---|
| 1 . | 80°Cx8Hr |
| 2 . | 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUMILITE® PL-1187 | Sumitomo Bakelite Co., Ltd. | Phenolic | SUMILITE® |
| Capran Medallion庐 MT-2500 | Honeywell | Nylon 6 | Capran Medallion® |
| Formolene® 5140N | Formosa Plastics Corporation, U.S.A. | PP Homopolymer | Formolene® |
| Hylon® N2040ML | Ravago Manufacturing Americas, LLC | Nylon 6 | Hylon® |
| LUVOCOM® 1-RG 3 | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |