Premi-Glas® 1200H-22
| Category: | TS, Unspecified , Thermoset, Unspecified |
| Manufacturer: | Premix, Inc. |
| Trademark: | Premi-Glas® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gf6K1H_Premi-Glas-1200H-22.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Premi-Glas® 1200H-22 is a fiberglass reinforced thermoset sheet molding compound for general purpose applications requiring thermal stability and stiffness. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| UL File Number |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.70 to 1.85 | g/cm³ | |
| Molding Shrinkage - Flow | 0.15 to 0.30 | % | |
| Outdoor Suitability | f1 | UL 746C |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 12000 | MPa | ASTM D638 |
| Tensile Strength | 55.0 | MPa | ASTM D638 |
| Flexural Modulus | 10000 | MPa | ASTM D790 |
| Flexural Strength | 135 | MPa | ASTM D790 |
| Compressive Strength | 165 | MPa | ASTM D695 |
| Poisson's Ratio | 0.30 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 650 | J/m | ASTM D256 |
| Unnotched Izod Impact | 850 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CLTE | |||
| Flow 1 | 2.5E-5 | cm/cm/°C | |
| Transverse 2 | 3.5E-5 | cm/cm/°C | |
| Thermal Conductivity | 0.30 | W/m/K | |
| RTI Elec | 130 | °C | UL 746 |
| RTI Imp | 130 | °C | UL 746 |
| RTI Str | 130 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 15 | kV/mm | ASTM D149 |
| Arc Resistance | 180 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 150 | °C | |
| Injection Pressure | 3.50 to 6.50 | MPa |
| Note Message | |
|---|---|
| 1 . | XY Direction |
| 2 . | Z Direction |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VENELENE® 11S1 | Poliolefinas Internacionales, C.A. (Polinter) | LLDPE | VENELENE® |
| ISPLEN® PR 230 C1E | REPSOL | PP Random Copolymer | ISPLEN® |
| LNP™ STAT-KON™ OE004AE compound | SABIC Innovative Plastics | PPS, Branched | LNP™ STAT-KON™ |
| LNP™ STAT-KON™ OX00428 compound | SABIC Innovative Plastics | PPS, Linear | LNP™ STAT-KON™ |
| LNP™ LUBRICOMP™ QL002 compound | SABIC Innovative Plastics | Nylon 610 | LNP™ LUBRICOMP™ |