Order Products : sales@su-jiao.com
Moplen RP325M
| Category: | PP Random Copolymer , Polypropylene Random Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Moplen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gdf2Gc_Moplen-RP325M.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
"Moplen" RP325M is a controlled rheology slightly propylene random copolymer for manufacturing high transparent cast films. The product contains slip- and antiblock agents. It exhibits very good optical properties and good heat weldability. Main applications are packaging of foodstuffs such as sweets, pasta, biscuits and snacks, packaging of books, stationary, blankets, shirts and hosiery. "Moplen" RP325M is suitable for food contact. For regulatory information please refer to "Moplen" RP325M Product Stewardship Bulletin ( PSB ). |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 900 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 25.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 11 | % | ISO 527-2/50 |
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic | 0.20 | ||
| vs. Itself - Static | 0.20 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Secant Modulus - MD 1(50 µm) | 640 | MPa | ASTM D882 |
| Tensile Strength - MD 2 | ASTM D882 | ||
| Yield, 50 µm | 19.4 | MPa | |
| Break, 50 µm | 38.0 | MPa | |
| Tensile Elongation - MD 3 | ASTM D882 | ||
| Yield, 50 µm | 6.7 | % | |
| Break, 50 µm | 760 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| 0°C | 1.4 | kJ/m² | |
| 23°C | 4.5 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 68.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 130 | °C | ISO 306/A50 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.0 µm) | 89 | ASTM D2457 | |
| Haze (50.0 µm) | < 1.0 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 30 mm/min |
| 2 . | 500 mm/min |
| 3 . | 500 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| AKROMID® B3 LA black (4056) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| ASTAMID™ KB3EG5 | Marplex Australia Pty. Ltd. | Nylon 6 | ASTAMID™ |
| DuraElast 1513-7 | Evermore Chemical Industry Co., Ltd. | TPU-Polyether | DuraElast |
| InnoPlus LD2420D | PTT Global Chemical Public Company Limited | LDPE | InnoPlus |
| LNP™ THERMOCOMP™ RC008 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |