Nylene® 406

Category:	Nylon 6 , Polyamide 6
Manufacturer:	Custom Resins Group
Trademark:	Nylene®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	gdG4ux_Nylene-406.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

General purpose, fast cycling molding resin

Crystallization initiators provide fast molding cycles through rapid melt set-up

Parts molded from 406 have better dimensional stability at moisture equilibrium than parts molded from conventional nylon

Optimum processing conditions should provide a melt temperature of 450°F-470°F at the nozzle

General Information
Features	Fast Molding Cycle General Purpose Good Dimensional Stability
Processing Method	Injection Molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.13	g/cm³	ASTM D792
Molding Shrinkage - Flow	0.90	%	ASTM D955

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength (23°C)	75.2	MPa	ASTM D638
Tensile Elongation (Break, 23°C)	25	%	ASTM D638
Flexural Modulus (23°C)	2760	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (23°C)	43	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load			ASTM D648
0.45 MPa, Unannealed	182	°C
1.8 MPa, Unannealed	71.1	°C
Peak Melting Temperature	216	°C	ASTM D3418

Flammability	Nominal Value		Test Method
Flame Rating (1.47 mm)	V-2		UL 94

Injection	Nominal Value	Unit
Processing (Melt) Temp	232 to 243	°C

Resin Grade	Manufacturer	Category	Trademark
Maxxam™ PPC-40C Nat	PolyOne Corporation	PP Copolymer	Maxxam™
Wellamid® GF20-60 XE-N	Wellman Engineering Resins	Nylon 6	Wellamid®
Karina WHITE PVC COMPOUND 750-10/1-C-IS	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina
OmniTech™ CPP XE72A BK17	OMNI Plastics, LLC	PP Copolymer	OmniTech™
Eco-FUDOWLITE® F8000	Fudow Co., Ltd.	Phenolic	Eco-FUDOWLITE®