MEGOLON+ S800 is a thermoplastic, halogen free, fire retardant high-speed cable sheathing compound for general-purpose applications. This product exhibits excellent processing characteristics including the ability to extrude at very high speeds and has been specifically designed to allow cable manufacturers to maximise volumetric output and efficiency

APPLICATIONS

UK: BS 7878 : 7 (HD 624.7 S1)

Germany: DIN VDE 0207, part 24, type HM2

Also complies with BS7655 6.1 Grades LTS1 and LTS 3

Designed to meet the demands of the data and communication cable market

Also suitable for low voltage cable applications

General Information
Features	Flame Retardant General Purpose Good Colorability Good Processability Good Surface Finish Halogen Free Moisture Resistant
Uses	Cable Jacketing Communication Wire Insulation General Purpose Low Voltage Insulation
Agency Ratings	BS 7655:6.1 Type LTS 1 BS 7655:6.1 Type LTS 3 BS 7878:7 (HD 624.7 S1) DIN VDE 0207, Part 24, Type HM2 IEC 60332-1
Forms	Pellets
Processing Method	Extrusion

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.50	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (150°C/21.6 kg)	10	g/10 min	ISO 1133

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D)	54		ASTM D2240

Mechanical	Nominal Value	Unit	Test Method
Tensile Stress
-- ¹	13.2	MPa	IEC 60811-1-2
--	12.0	MPa	IEC 60811-1-1
Tensile Strain
Break ²	130	%	IEC 60811-1-2
Break	150	%	IEC 60811-1-1
Elongation at Break
after 4 hours, in ASTM #2 Oil : 70°C	160	%
after 4 hours, in Diesel : 70°C	44	%
after 4 hours, in SAE 20 Oil : 70°C	100	%
after 7 days, in ASTM #2 Oil : 23°C	200	%
after 7 days, in Diesel : 23°C	140	%
Tensile Strength
after 4 hours, in ASTM #2 Oil : 70°C	7.00	MPa
after 4 hours, in Diesel : 70°C	2.00	MPa
after 4 hours, in SAE 20 Oil : 70°C	5.00	MPa
after 7 days, in ASTM #2 Oil : 23°C	12.1	MPa
after 7 days, in Diesel : 23°C	10.6	MPa

Thermal	Nominal Value	Unit	Test Method
Hot Pressure Test (80°C)	30	%	IEC 60811-3-1

Electrical	Nominal Value	Unit	Test Method
Insulation Resistance			BS 6469 99.2
20°C	5.0E+14	ohms·cm
after 28 days immersion in water : 20°C	5.0E+12	ohms·cm

Flammability	Nominal Value	Unit	Test Method
Acid Gas Emission Conductivity	5.00	µS/cm	IEC 60754-2
Acid Gas Emission pH	5.50		IEC 60754-2
Flammability Temperature Index	345	°C	ISO 4589-3

Additional Information	Nominal Value	Unit	Test Method
Halogen Acid Gas Evolution	0.0	%	IEC 60754-1

Extrusion	Nominal Value	Unit
Draw Down	1.5:1.0
Extruder Screw Compression Ratio	1.0:1.0 to 2.0:1.0

Elastomers	Nominal Value	Unit	Test Method
Tear Strength	8.50	kN/m	BS 6469 99.1

Aging	Nominal Value	Unit	Test Method
Change in Tensile Strength in Air (100°C, 168 hr)	10	%
Change in Tensile Strain at Break in Air (100°C, 168 hr)	-15	%
Change in Tensile Stress
23°C, 168 hr, in ASTM #2 Oil	0.50	%
23°C, 168 hr, in Diesel	-12	%
70°C, 4 hr, in ASTM #2 Oil	-42	%
70°C, 4 hr, in Diesel	-83	%
70°C, 4 hr, in SAE 20 Oil	-58	%
70°C, 168 hr, in Water	-14	%	BS 6469 99.1
Change in Tensile Strain at Break
23°C, 168 hr, in ASTM #2 Oil	33	%
23°C, 168 hr, in Diesel	-10	%
70°C, 4 hr, in ASTM #2 Oil	7.0	%
70°C, 4 hr, in Diesel	-71	%
70°C, 4 hr, in SAE 20 Oil	-32	%
70°C, 168 hr, in Water	-25	%	BS 6469 99.1

Flammability	Nominal Value	Unit	Test Method
Oxygen Index	30	%	ISO 4589-2

Extrusion	Nominal Value	Unit
Drying Temperature	60.0 to 70.0	°C
Cylinder Zone 1 Temp.	135	°C
Cylinder Zone 2 Temp.	140	°C
Cylinder Zone 3 Temp.	145	°C
Cylinder Zone 4 Temp.	150	°C
Cylinder Zone 5 Temp.	160	°C
Melt Temperature	165 to 175	°C
Die Temperature	165	°C

Note Message
1 .	after 7 days at 100°C
2 .	after 7 days at 100°C

Resin Grade	Manufacturer	Category	Trademark
VITAMIDE® BG32NT6719	Jackdaw Polymers	Nylon 6	VITAMIDE®
Yuyao PBT 4029G30	Yuyao Tenglong Plastics Co., Ltd.	PBT	Yuyao PBT
Fiberfil® M-2149	Fiberfil® Engineered Plastics Inc.	PP Homopolymer	Fiberfil®
GAPEX® HPP40GR21HB BLACK	Ferro Corporation	PP Homopolymer	GAPEX®
LNP™ THERMOCOMP™ MFB22EXJ compound	SABIC Innovative Plastics	PP, Unspecified	LNP™ THERMOCOMP™