Axiall PVC UV-6676
| Category: | PVC, Rigid , Rigid Polyvinyl Chloride |
| Manufacturer: | Axiall Corporation |
| Trademark: | Axiall PVC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gcXAGw_Axiall-PVC-UV-6676.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Georgia Gulf UV-6676 is a weatherable, high flow injection molding compound, specially formulated for outdoor UV exposure. This compound was designed to be used in various accessory parts, such as fence post caps, rain gutter parts, deck parts, etc. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.40 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.30 - 0.40 | % | ASTM D955 |
| Outdoor Suitability | f2 | UL 746C |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 97 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2210 | MPa | ASTM D638 |
| Tensile Strength | 40.0 | MPa | ASTM D638 |
| Flexural Modulus | 2280 | MPa | ASTM D790 |
| Flexural Strength | 65.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -20°C, 3.18 mm | 53 | J/m | ASTM D256 |
| 23°C, 3.18 mm | 960 | J/m | ASTM D256 |
| Dart Drop Impact (23°C) | 14.7 | J | ASTM D3029 |
| Drop Impact Resistance (23°C) | 89.0 | J/cm | ASTM D4226 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 72.0 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 70.0 | °C | ASTM D648 |
| RTI Elec (1.50 mm) | 85.0 | °C | UL 746 |
| RTI Imp (1.50 mm) | 90.0 | °C | UL 746 |
| RTI (1.50 mm) | 85.0 | °C | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 5VA | UL 94 | |
| Oxygen Index | 35 | % | ASTM D2863 |
| Additional Information |
|---|
| Flow Ratio, Georgia Gulf Test Method, Distance/Wall Thickness, 390-400°F: 230 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 65.6 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Drying Time, Maximum | 6.0 | hr | |
| Suggested Shot Size | 35 - 75 | % | |
| Suggested Max Regrind | 50 | % | |
| Rear Temperature | 163 | °C | |
| Middle Temperature | 174 - 191 | °C | |
| Front Temperature | 182 - 193 | °C | |
| Nozzle Temperature | 177 - 193 | °C | |
| Processing (Melt) Temp | 202 - 210 | °C | |
| Mold Temperature | 15.6 - 48.9 | °C | |
| Injection Pressure | 82.7 - 138 | MPa | |
| Holding Pressure | 48.3 - 82.7 | MPa | |
| Back Pressure | 0.345 - 1.38 | MPa | |
| Screw Speed | 25 - 80 | rpm | |
| Clamp Tonnage | 3.4 | kN/cm² | |
| Screw L/D Ratio | 16.0:1.0 to 24.0:1.0 | ||
| Screw Compression Ratio | 1.5:1.0 to 2.5:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadrant EPP Nylatron® LFG Nylon | Quadrant Engineering Plastic Products | Nylon 6 | Quadrant EPP |
| Sup-tech B9260 | Shanghai Suptech Engineering Plastics Co. Ltd. | Nylon 6 | Sup-tech |
| Fainplast PVC PG 86/AF | Fainplast Compounds S.r.l | PVC+NBR | Fainplast PVC |
| Ferro PP LPP30BC53WH | Ferro Corporation | PP Homopolymer | Ferro PP |
| KW Plastics KW 308A | KW Plastics | PP Impact Copolymer | KW Plastics |