VENYL SFRT208 - 8229
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | AD majoris |
| Trademark: | VENYL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gbhVZP_VENYL-SFRT208---8229.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
VENYL SFRT208 - 8229 is a halogen free flame retardant compounds UL 94 V2 with 25% mineral filled polyamide 6 intended for Injection moulding. APPLICATIONS VENYL SFRT208 - 8229 has been developed especially for very demanding applications in automotive industry and electrical parts. Products requiring excellent combination between thermal and mechanical properties. VENYL SFRT208 - 8229 is available in natural (VENYL SFRT208) but other colours can be provided on request. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.35 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.60 to 1.0 | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.9 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5200 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 70.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.5 | % | ISO 527-2 |
| Flexural Modulus | 6350 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 25 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 205 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 115 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 220 | °C | ISO 3146 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-2 | UL 94 | |
| Glow Wire Flammability Index (1.00 mm) | 960 | °C | IEC 60695-2-12 |
| Oxygen Index | 30 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 235 to 240 | °C | |
| Middle Temperature | 240 to 250 | °C | |
| Front Temperature | 250 to 260 | °C | |
| Nozzle Temperature | 250 to 260 | °C | |
| Mold Temperature | 80.0 to 100 | °C | |
| Injection Pressure | 80.0 to 100 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 50.0 to 70.0 | MPa | |
| Screw L/D Ratio | 15.0:1.0 to 20.0:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Resinoid 1322 | Resinoid Engineering Corporation | Phenolic | Resinoid |
| Sinpolene FRF2074 | Teknor Apex Asia Pacific PTE. LTD. | PP, Unspecified | Sinpolene |
| EPDM 720P | The Dow Chemical Company | EPDM | EPDM |
| Kepital® TX-21 | Korea Engineering Plastics Co., Ltd | Acetal (POM) Copolymer | Kepital® |
| Sylvin 7833-85 Blue 8431 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |