PROTEQ™ C30US
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | PROTEQ™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gZt8pU_PROTEQ-C30US.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PROTEQ™ C30US is a Polypropylene copolymer which has been heat and UV stabilised with antistatic treatment. PROTEQ™C30US is designed for difficult to fill automotive applications requiring a balance of toughness, rigidity, heat resistance, marr resistance and even surface appearance. Typical applications are automotive interior trim. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.900 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 30 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 1.7 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 70 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.20 mm) | 26.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 90 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 1100 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 36.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 75 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 78.0 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 50.0 | °C | |
| CLTE - Flow | 9.0E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature (1.60 mm) | 550 | °C | AS/NZS 60695 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 to 90.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 195 to 215 | °C | |
| Middle Temperature | 205 to 225 | °C | |
| Front Temperature | 215 to 235 | °C | |
| Processing (Melt) Temp | 220 to 270 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Injection Pressure | 60.0 to 140 | MPa | |
| Injection Rate | Moderate | ||
| Screw Speed | 40 to 60 | rpm | |
| Clamp Tonnage | 3.0 to 6.0 | kN/cm² |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Aarolene® ARPP H 200-1 | Aaron Industries Corp. | PP Homopolymer | Aarolene® |
| Ferro PP LPP40BD22WH | Ferro Corporation | PP Homopolymer | Ferro PP |
| K-Bin Rigid PVC KB-5026 | K-Bin, Inc. | PVC, Unspecified | K-Bin Rigid PVC |
| Jam 15YF8 | Jam Petrochemical Company | LLDPE | Jam |
| LNP™ LUBRICOMP™ KFL23LH compound | SABIC Innovative Plastics | Acetal (POM) Copolymer | LNP™ LUBRICOMP™ |