Braskem PP CP 141
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Braskem |
| Trademark: | Braskem PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gZpT8k_Braskem-PP-CP-141.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description: CP 141 is a high melt flow rate heterophasic copolymer specially designed to achieve high productivity on thin-walled parts with very easy mould filling and high speed injection moulding. This product features an excelent impact strenght at low temperatures and high flow. Applications: Household; Thin-walled articles. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.900 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 43 | g/10 min | ASTM D1238, ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| R-Scale, Injection Molded | 83 | ASTM D785 | |
| R-Scale | 83 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, Injection Molded) | 26.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Yield, Injection Molded) | 6.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| 1% Secant : Injection Molded | 1300 | MPa | ASTM D790 |
| Injection Molded | 1250 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| -20°C, Injection Molded | 45 | J/m | ASTM D256 |
| 23°C, Injection Molded | 90 | J/m | ASTM D256 |
| -20°C, Injection Molded | 4.4 | kJ/m² | ISO 180 |
| 23°C, Injection Molded | 7.3 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, Injection Molded | 110 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 110 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, Injection Molded | 57.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 57.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 149 | °C | ISO 306/A, ASTM D1525 1 |
| Note Message | |
|---|---|
| 1 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Arak HDPE BL1 | Shazand (Arak) Petrochemical Corporation | HDPE | Arak HDPE |
| Exelene® PVC K65 | Montachem International, Inc. | PVC Homopolymer | Exelene® PVC |
| Elastron® G G501.A23.N | Elastron USA, Inc. | SEBS | Elastron® G |
| SABIC® EPDM 657 | Saudi Basic Industries Corporation (SABIC) | EPDM | SABIC® EPDM |
| Softell DKG100N | LyondellBasell Industries | TPO (POE) | Softell |