Maxxam™ PPC-20G Black
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Maxxam™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gZB5dC_Maxxam-PPC-20G-Black.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polypropylene and Polyethylene Based Maxxam™The product line is suitable for a variety of applications and performance requirements. After the standard product is mixed with calcium carbonate, glass and talcum powder, all the properties are ideal, including rigidity, durability, impact resistance and heat resistance. Customized products have many uses, such as: ultraviolet stabilizer, heat stabilizer, color customization, impact resistance products, etc. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.03 | g/cm³ | ASTM D792 |
| Specific Volume | 0.972 | cm³/g | ASTM D792 |
| Melt Mass-Flow Rate (MFR) 1(230°C/2.16 kg) | 4.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.20 - 0.50 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2(Yield) | 50.0 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 9.0 | % | ASTM D638 |
| Flexural Modulus | 3030 | MPa | ASTM D790 |
| Flexural Strength | 62.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm, Injection Molded) | 64 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 3.18 mm) | 152 | °C | ASTM D648 |
| Additional Information |
|---|
| Product Code: EM10005762** |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 16.0 - 50.0 | °C |
| Note Message | |
|---|---|
| 1 . | Procedure A |
| 2 . | Type 1, 51mm/min |
| 3 . | Type 1, 51mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Topolymer® 5321-951E | Dongguan Top Polymer Enterprise | TPE | Topolymer® |
| XYRON™ X1508 | Asahi Kasei Chemicals Corporation | PPE+PS | XYRON™ |
| Badamid® C70 | Bada AG | Nylon 66/6 | Badamid® |
| ELASTOSIL® RT 604 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® RT |
| Hanwha Total PE 610A | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | LDPE | Hanwha Total PE |