LNP™ LUBRICOMP™ EL002 compound
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gZ64Yl_LNP-LUBRICOMP-EL002-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* LUBRICOMP* EL002 is a compound based on Polyetherimide resin containing 10% PTFE. Added feature of this material is: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound EL-4020 Product reorder name: EL002 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- | 1.32 | g/cm³ | |
| -- | 1.31 | g/cm³ | |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.70 to 0.90 | % | |
| Across Flow : 24 hr | 0.80 to 1.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.20 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.30 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3450 | MPa | ASTM D638 |
| -- | 2750 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 103 | MPa | ASTM D638 |
| Yield 2 | 86.5 | MPa | ASTM D638 |
| Yield | 82.0 | MPa | ISO 527-2/5 |
| Break 3 | 76.9 | MPa | ASTM D638 |
| Break | 78.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 6.5 | % | ASTM D638 |
| Yield | 6.3 | % | ISO 527-2/5 |
| Break 5 | 14 | % | ASTM D638 |
| Break | 10 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 3040 | MPa | ASTM D790 |
| -- | 3450 | MPa | ASTM D790 |
| -- 7 | 2810 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 145 | MPa | ASTM D790 |
| -- | 108 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.33 | ||
| vs. Itself - Static | 0.30 | ||
| Wear Factor - Washer | 185 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 53 | J/m | ASTM D256 |
| 23°C 8 | 5.2 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 580 | J/m | ASTM D4812 |
| 23°C 9 | 38 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 6.10 | J | ASTM D3763 |
| -- | 1.38 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 203 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 10 | 201 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 193 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 186 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 4.8E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 4.7E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 343 to 354 | °C | |
| Middle Temperature | 354 to 366 | °C | |
| Front Temperature | 366 to 377 | °C | |
| Processing (Melt) Temp | 360 to 366 | °C | |
| Mold Temperature | 121 to 149 | °C | |
| Back Pressure | 0.344 to 0.689 | MPa | |
| Screw Speed | 60 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRIREX® Compound 3025N1 | Samyang Corporation | PC | TRIREX® Compound |
| AMTOPP BFP35 | Inteplast Group | PP, Unspecified | AMTOPP |
| Fainplast PVC MRK 267 | Fainplast Compounds S.r.l | PVC, Rigid | Fainplast PVC |
| ESTOPLAST EP 40002NN01 | Ester Industries Ltd. | PBT | ESTOPLAST EP |
| TOTAL Polystyrene Crystal 525L | TOTAL Refining & Chemicals | PS (GPPS) | TOTAL Polystyrene |