Novablend™ 6602
| Category: | PVC, Rigid , Rigid Polyvinyl Chloride |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Novablend™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gYfpTi_Novablend-6602.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Novablend 6602 is a rigid, opaque PVC for molding compounds. This product has high impact, excellent indoor/outdoor weathering, high flow, and good processing characteristics.Applications includes: Electrical,Business machines,Telecommunications, Multi Purpose. |
| General Information | |
|---|---|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.35 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.20 to 0.50 | % | ASTM D955 |
| Outdoor Suitability | f1 | UL 746C |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 15 sec) | 81 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2450 | MPa | ASTM D638 |
| Tensile Strength | 45.5 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 32 | % | ASTM D638 |
| Flexural Modulus | 2520 | MPa | ASTM D790 |
| Flexural Strength | 70.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm, Injection Molded) | 640 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm 2 | 67.2 | °C | |
| 0.45 MPa, Annealed, 3.18 mm 3 | 70.6 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm 4 | 57.0 | °C | |
| 1.8 MPa, Annealed, 3.18 mm 5 | 68.3 | °C | |
| RTI Elec 6 | 105 | °C | UL 746 |
| RTI Elong 7 | 105 | °C | UL 746 |
| RTI Str 8 | 105 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating 9(1.80 mm, All) | 5VA | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 199 to 204 | °C |
| Note Message | |
|---|---|
| 1 . | Type I |
| 2 . | 67 degr. C. |
| 3 . | 71 degr. C. |
| 4 . | 57 degr. C. |
| 5 . | 68 degr. C. |
| 6 . | 105 deg. C. |
| 7 . | 105 degr. C. |
| 8 . | 105 degr. C. |
| 9 . | Also UL 94 V-O @ 0.059 in thick. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Premier LH01019 - B | Premier Polymers, LLC. | LLDPE | Premier |
| PRIMALENE WPP411C | Southern Polymer, Inc. | PP Random Copolymer | PRIMALENE |
| SEPTON™ HG252 | Kuraray Co., Ltd. | SEEPS | SEPTON™ |
| Starflam PZ0062E | Eurostar Engineering Plastics | Nylon 6 | Starflam |
| POLYCASA® ACRYL G 88 E | Polycasa | Acrylic (PMMA) | POLYCASA® ACRYL |