Halene L 92001S
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Haldia Petrochemicals Ltd. |
| Trademark: | Halene L |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gYX6Rb_Halene-L-92001S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
92001S is a 1-Hexene LLDPE copolymer blown film grade produced by the Spherilene Technology. This grade can be used in Multilayer Packaging Film Applications. 92001S is additivated with slip and antiblocking additives for excellent openability and slip properties. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 0.920 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested 2 | 55 | µm | |
| Tensile Strength 3 | ASTM D882 | ||
| MD : Yield, 55 µm | 10.0 | MPa | ASTM D882 |
| TD : Yield, 55 µm | 10.0 | MPa | ASTM D882 |
| MD : Break, 55 µm | 31.0 | MPa | ASTM D882 |
| TD : Break, 55 µm | 26.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 55 µm | 950 | % | ASTM D882 |
| TD : Break, 55 µm | 1100 | % | ASTM D882 |
| Dart Drop Impact 4 | 280 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 55 µm | 550 | g | ASTM D1922 |
| TD : 55 µm | 800 | g | ASTM D1922 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gloss (60°) | 80 | ASTM D2457 |
| Additional Information |
|---|
| Barrel Temperature: 180 - 200 °CBlow up Ratio: 2.0 - 3.0Die Gap: 2.0 - 2.5 mm |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 - 210 | °C |
| Note Message | |
|---|---|
| 1 . | 23°C |
| 2 . | BUR - 2.5, Die Gap - 2.5 mm |
| 3 . | 500 mm/min |
| 4 . | F50, 38 mm Dart, 66-cm. Height |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| DOW™ LLDPE DFDA-7059 NT 7 | The Dow Chemical Company | LLDPE | DOW™ LLDPE |
| Niche PPHM6BK | Niche Polymer, LLC | PP Homopolymer | Niche |
| Double Elephant SX-302 | Suzhou Double Elephant Optical Material Co., LTD. | Acrylic (PMMA) | Double Elephant |
| LNP™ LUBRICOMP™ MG004 compound | SABIC Innovative Plastics Europe | PP, Unspecified | LNP™ LUBRICOMP™ |
| LONGLITE® LCP LCP-300 B4G | CCP Group | LCP | LONGLITE® LCP |