Adiprene® L 367
| Category: | PUR-Ether/TDI , Polyurethane (Polyether, TDI) |
| Manufacturer: | Chemtura |
| Trademark: | Adiprene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gYETTx_Adiprene-L-367.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ADIPRENE L 367 is a polyether-based liquid urethane polymer which is readily processable by conventional hand and machine mixing techniques. ADIPRENE L 367 produces high quality elastomers in the 46-50 durometer D hardness range when cured with 4,4'-methylene-bis (2-chloroaniline) or CAYTUR® 21DA urethane curative. These tough, highly resilient elastomers have many unique features:
These properties suggest the use of ADIPRENE L 367 in applications such as wheels, small rolls, or spraying. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 48 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% Strain | 12.4 | MPa | |
| 300% Strain | 30.3 | MPa | |
| Tensile Strength | 42.1 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 350 | % | ASTM D412 |
| Tear Strength (Split) | 21 | kN/m | ASTM D470 |
| Compression Set (70°C, 22 hr) | 28 | % | ASTM D395B |
| Bayshore Resilience | 40 | % | ASTM D2632 |
| Clash-Berg Modulus | ASTM D1043 | ||
| -57°C | 324 | MPa | |
| -40°C | 65.7 | MPa | |
| -18°C | 43.4 | MPa | |
| 24°C | 37.9 | MPa |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Weight: 19 | ||
| Resin | Mix Ratio by Weight: 100 | ||
| Pot Life | 2.0 | min | |
| Post Cure Time (70°C) | 16 | hr |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Abrasion Index - NBS | 290 |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Curing Time (100°C) | 1.0 | hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen HP325M | LyondellBasell Industries | PP Homopolymer | Moplen |
| Tislamid® PA66 PA66 UNR FR HF | Tisan | Nylon 66 | Tislamid® PA66 |
| Akulon® F130-C2 | DSM Engineering Plastics | Nylon 6 | Akulon® |
| LNP™ LUBRICOMP™ IFP36 compound | SABIC Innovative Plastics | Nylon 612 | LNP™ LUBRICOMP™ |
| LNP™ THERMOCOMP™ RF007SXP compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |