LTP LTP8160
| Category: | PPS Alloy , Polyphenylene Sulfide Alloy |
| Manufacturer: | Chengdu Letian Plastics Co., Ltd |
| Trademark: | LTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gXWd4d_LTP-LTP8160.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LTP 8100 serials is reinforced composite materials with high performance based on polyolefin and PPS, and are extensively applied in injection mold to structure and parts of machine, electric appliance and automobiles. It is used to replace materials of PA PBT (PET), PPO (PPE), and PC/ABS serial. The LTP 8100 serials materials have the characteristics of high impact strength, high dimensional stability and low moisture absorption. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.32 | g/cm³ | ASTM D792 |
| Molding Shrinkage 1 | |||
| Across Flow : 3.00 mm | 0.80 | % | |
| Flow : 3.00 mm | 0.50 | % | |
| Water Absorption (Saturation) | 0.30 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 60.0 | MPa | GB/T 1040 |
| Tensile Strain (Break) | 12 | % | GB/T 1040 |
| Flexural Stress | 100 | MPa | GB/T 1042 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 15 | kJ/m² | GB/T 1043 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | > 165 | °C | GB/T 1634 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 2.0E+15 | ohms | GB/T 1410 |
| Volume Resistivity | 5.0E+14 | ohms·cm | GB/T 1410 |
| Dielectric Strength | 17 | kV/mm | ASTM D149 |
| Dielectric Constant | GB/T 1409 | ||
| 25°C, 1 kHz | 3.20 | ||
| 25°C, 1 MHz | 3.20 | ||
| Dissipation Factor | GB/T 1409 | ||
| 25°C, 1 kHz | 3.0E-3 | ||
| 25°C, 1 MHz | 3.0E-3 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 80x80x3 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sipolprene® 63210 W | SIPOL S.p.A | TPC-ET | Sipolprene® |
| Sylvin 2956-80 Green 3171 | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |
| apilon 52bio® DB 40 | API SpA | TPU-Polyester | apilon 52bio® |
| Emulprene® 1011CR | INSA | SBR, Emulsion | Emulprene® |
| RONFALIN® ABS 1314 GB 10 | A. Schulman Europe | ABS | RONFALIN® |