4POM® 23I00000
| Category: | Acetal (POM) Homopolymer , Acetal (POM) Homopolymer |
| Manufacturer: | 4Plas |
| Trademark: | 4POM® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gWvNmR_4POM-23I00000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 4POM 23I00000 is a MFI 2.5 Unfilled POM |
| General Information | |
|---|---|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.41 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.5 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2800 | MPa | ISO 527-2/5 |
| Tensile Stress (Break, 23°C) | 67.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 15 | % | ISO 527-2/5 |
| Flexural Modulus 1(23°C) | 2500 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.0 | kJ/m² | ISO 179/B |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 156 | °C | ISO 75-2/B |
| Melting Temperature 2 | 165 | °C | ISO 11357 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 120 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 180 - 220 | °C | |
| Mold Temperature | 60.0 - 100 | °C | |
| Injection Rate | Moderate-Fast | ||
| Holding Pressure | 80.0 - 100 | MPa | |
| Screw Speed | 300 | rpm |
| Injection instructions |
|---|
| Feed Throat Temperature: 30 - 50 °CBack Pressure: Low |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 10 K/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Stanyl® TW363 | DSM Engineering Plastics | Nylon 46 | Stanyl® |
| Moldex® QS986A/M151 | Mitsubishi Chemical Corporation | Polyolefin, Unspecified | Moldex® |
| CYCOLOY™ HCX1640 resin | SABIC Innovative Plastics Europe | PC+ABS | CYCOLOY™ |
| TechnoElast V D4000 I 2 sw | TechnoCompound GmbH | TPE | TechnoElast |
| OTECH TPE OTR7598 - Profile | OTECH Corporation | TPE | OTECH TPE |