RAMOFIN PPH343T4BK10-1
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Polyram Ram-On Industries |
| Trademark: | RAMOFIN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gWdg4o_RAMOFIN-PPH343T4BK10-1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 20% MINERAL FILLED, HEAT RESISTANT POLYPROPYLENE FOR INJECTION MOLDING APPLICATIONS. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.08 | g/cm³ | ASTM D792 |
| -- | 1.06 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow | 1.1 - 1.5 | % | ASTM D955 |
| -- | 1.1 - 1.5 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2500 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Yield) | 30.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 25 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 2200 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | 55.0 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.8 | kJ/m² | ISO 179 |
| Notched Izod Impact (23°C) | 30 | J/m | ASTM D256 |
| Unnotched Izod Impact Strength (23°C) | 40 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 154 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, not annealed | 82.0 | °C | ASTM D648, ISO 75-2/A |
| Melting Temperature | 168 | °C | ISO 11357-3, ASTM D3418 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 | |
| Flammability | 22 | mm/min | FMVSS 302 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 190 - 220 | °C | |
| Middle Temperature | 200 - 225 | °C | |
| Front Temperature | 205 - 230 | °C | |
| Mold Temperature | 30.0 - 65.0 | °C | |
| Injection Pressure | 70.0 - 105 | MPa | |
| Holding Pressure | 35.0 - 70.0 | MPa | |
| Back Pressure | 0.350 - 0.700 | MPa | |
| Screw Speed | 60 - 90 | rpm |
| Injection instructions |
|---|
| Fill Speed: 25 to 50 mm/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Telcar® TL-81-D920-A | Teknor Apex Company | TPE | Telcar® |
| HAIPLEN EP90 T8 | Taro Plast S.p.A. | PP Copolymer | HAIPLEN |
| Hifax TYC 773X | LyondellBasell Industries | TPO (POE) | Hifax |
| Lion Idemitsu Composites PPS Y531F1 | Lion Idemitsu Composites Co., Ltd. | PPS | Lion Idemitsu Composites PPS |
| Karina CLEAR PVC COMPOUND -E 80/278-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |