NEXT REPROCESSED PPC SB891-300R
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | NEXT Specialty Resins, Inc. |
| Trademark: | NEXT REPROCESSED |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gWdSA2_NEXT-REPROCESSED-PPC-SB891-300R.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NEXT REPROCESSED PPC SB891-300R is a Polypropylene Impact Copolymer (PP Impact Copolymer) material. It is available in North America. Important attributes of NEXT REPROCESSED PPC SB891-300R are:
Typical application of NEXT REPROCESSED PPC SB891-300R: Automotive |
| General Information | |
|---|---|
| Recycled Content |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.900 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 30 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 90 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 20.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 5.0 | % | ASTM D638 |
| Flexural Modulus | 1310 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 64 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 96.1 | °C | ASTM D648 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Safron® H506-04 | Safripol (PTY) LTD | PP Homopolymer | Safron® |
| SynPlast™ NOTM-E | PolyOne Corporation | Tri (n-octyl) Trimellitate | SynPlast™ |
| Toraypef® 15020 AP51 | Toray Resin Company | Polyolefin, Unspecified | Toraypef® |
| Vyncolit® 4221XB | Vyncolit N.V. | Phenolic | Vyncolit® |
| Lupoy® SC3154 | LG Chem Ltd. | PC | Lupoy® |