LNP™ STAT-KON™ MFD02 compound
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gW42HV_LNP-STAT-KON-MFD02-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON MFD02 is a compound based on Polypropylene resin containing 10% Glass Fiber. Added features of this material include: Electrically Conductive. Also known as: LNP* STAT-KON* Compound MF-10 Product reorder name: MFD02 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 1.1 to 1.3 | % | ASTM D955 |
| Across Flow : 24 hr | 1.1 to 1.3 | % | ASTM D955 |
| Across Flow : 24 hr | 1.2 | % | ISO 294-4 |
| Flow : 24 hr | 1.2 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2760 | MPa | ASTM D638 |
| -- | 2430 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 28.3 | MPa | ASTM D638 |
| Yield | 28.0 | MPa | ISO 527-2 |
| Break | 20.7 | MPa | ASTM D638 |
| Break | 23.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 3.2 | % | ASTM D638 |
| Yield | 2.9 | % | ISO 527-2 |
| Break | 6.1 | % | ASTM D638 |
| Break | 4.2 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2070 | MPa | ASTM D790 |
| -- | 2200 | MPa | ISO 178 |
| Flexural Stress | 43.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 130 | J/m | ASTM D256 |
| 23°C 2 | 15 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 380 | J/m | ASTM D4812 |
| 23°C 3 | 28 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 16.7 | J | ASTM D3763 |
| -- | 11.9 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 134 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 4 | 127 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 85.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 5 | 81.0 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -40 to 40°C | 1.0E-4 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Transverse : -40 to 40°C | 6.5E-5 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 6.4E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 10 to 1.0E+3 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 193 to 204 | °C | |
| Middle Temperature | 216 to 227 | °C | |
| Front Temperature | 238 to 249 | °C | |
| Processing (Melt) Temp | 227 to 249 | °C | |
| Mold Temperature | 32.2 to 48.9 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ColorRx® PC-2500RXR | LTL Color Compounders, Inc. | PC | ColorRx® |
| HAIPLEN H150 T8 | Taro Plast S.p.A. | PP Homopolymer | HAIPLEN |
| Hanwha Total PP TB54I | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| Hylac® GP45 | Ravago Manufacturing Americas, LLC | ABS | Hylac® |
| Karina CLEAR PVC COMPOUND 95/222-D-AT-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |