CYCOLAC™ INP572 resin
| Category: | ABS+SAN , Acrylonitrile Butadiene Styrene + SAN |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | CYCOLAC™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gVh2dL_CYCOLACINP572resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High molecular weight SAN, functions as a carrier resin for color concentrates. Can be used as compounding additives for polymer blends. Can be blended with high rubber graft modifier resins to produce customized ABS properties. Suitable for direct weather exposure. Provides excellent melt strength for extrusion, blow molding, or thermoforming applications |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.08 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 230°C/3.8 kg | 5.9 | g/10 min | ASTM D1238 |
| 220°C/10.0 kg | 16 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | |||
| 50.0mm span 1 | 3900 | MPa | ASTM D790 |
| -- 2 | 3460 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 92.0 | MPa | ISO 178 |
| Yield, 50.0mm span 3 | 134 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 1.4 | kJ/m² | ISO 179/2U |
| Notched Izod Impact | |||
| 23°C | 46 | J/m | ASTM D256 |
| -30°C 4 | 2.0 | kJ/m² | ISO 180/1A |
| 23°C 5 | 3.2 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 95.9 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 85.4 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 6 | 88.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 103 | °C | ISO 306/B50 |
| -- | 105 | °C | ISO 306/B120 |
| Note Message | |
|---|---|
| 1 . | 1.3 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 |
| 6 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Santoprene™ 111-45 | ExxonMobil Chemical | TPV | Santoprene™ |
| SHIN-A SAP-3208XP56 | SHIN-A T&C | Acrylic, Unspecified | SHIN-A |
| New-prene™ 6050B | Total Polymer Vision (Suzhou) Co., LTD | PP+EPDM | New-prene™ |
| Orgalloy® LE 60LM | Arkema | Nylon 6 Alloy | Orgalloy® |
| Plaslube® PC / ASA FR1508 UV | Techmer Engineered Solutions | ASA+PC | Plaslube® |